Hyunwoo Kim

Effects of P on amorphous chemical vapor deposition Ru-P alloy films for Cu interconnect liner applications

Amorphous Ru(P) films grown by chemical vapor deposition at 575 K using a single source precursor, cis-RuH2(P(CH3)3)4, or dual sources, Ru3(CO)12 and P(CH3)3 or P(C6H5)3, are studied. The phosphorus percentage affects the film microstructure, and incorporating >13% P resulted in amorphous Ru(P) films. While codosing P(CH3)3 with Ru3(CO)12 improves film step coverage, the most conformal Ru(P) film is obtained with cis-RuH2(P(CH3)3)4. A fully continuous 5 nm Ru(P) film is formed within 1 μm deep, 8:1 aspect ratio trenches. The barrier performance is tested using Cu/Ru/Si(100) stacks annealed at 575 K, and sheet resistance was used as a measure of barrier failure. Cu diffusivity in physical vapor deposition (PVD) Ru is approximated to be 6.6×10−17 cm2/s at 575 K, which indicates fast Cu diffusion along the grain boundaries. While 26 nm polycrystalline PVD Ru failed after 6 h annealing by Cu penetration, 28 nm amorphous Ru(P) survived after 67 h annealing. First principles density functional calculations sugg...

Behavior of Ga atoms on a tungsten surface

The variation of the work function and the preexponential term of the Fowler–Nordheim (FN) plots and field emission current from a Ga covered tungsten surface have been studied using a field emission microscope (FEM). The work function and preexponential terms both vary in the same way with coverage and desorption temperature. Both are decreased to 4.25 and −0.6 eV, respectively, at θ=0.2. In spite of a small decrease in work function, the field emission current decreased to about half of its initial value, because of a decrease in the emitting areas of the Ga covered tungsten surface. The polarizability of Ga, at this coverage, is also obtained as ∼3 A3.