The two aspects of a scanning tunneling microscopy tip, the macroscopic profile and the nanoscale apex, can be tailored by controlling the tension during electrochemical etching and the solution-electrode contact area via acetone vapor. The apex diameter is shown to be proportional to the square root of the tension, and is demonstrated over apex diameters of 150-500 nm. The apex was found to be created in four distinct shapes where a secondary etching can reshape the tip into a single geometry. Improvement in tip height and stability of the profile are demonstrated versus a non-acetone fabrication control.

Magnetostrictive iron gallium thin films grown onto antiferromagnetic manganese nitride: Structure and magnetism

We report structural and magnetic properties of magnetostrictive Fe100−xGax (x ≈ 15) alloys when deposited onto antiferromagnetic manganese nitride and non-magnetic magnesium oxide substrates. From X-ray diffraction measurements, we find that the FeGa films are single crystalline. Scanning tunneling microscopy imaging reveals that the surface morphologies are dictated by the growth temperature, composition, and substrate. The magnetic properties can be tailored by the substrate, as found by magnetic force microscopy imaging and vibrating sample magnetometry measurements. In addition to pronounced tetragonal deformations, depositing FeGa onto manganese nitride leads to the formation of stripe-like magnetic domain patterns and to the appearance of perpendicular magnetic anisotropy.