Surface engineering of electrospun fibers to optimize ion and electron transport in Li%2B battery cathodes.

This report documents research into the fabrication of Lithium Manganese Oxide (Spinel) (LMO) cathode material in the form of fibrous mats, the degradation process of this material in a battery electrolyte, the formation of core-shell coated fibers and the electrochemical properties of the active cathode core fiber. In practice, LMO experiences several degradation mechanisms ranging from capacity fading, the Jahn-Teller distortion phenomenon leading to dissolution in the electrolyte phase, and the formation of surface films by degradation of the electrolyte, and/or phase transitions at the surface to form Mn2O3. Density Functional Theory (DFT) was applied to model from first principles the interactions between the electrolyte and the surface leading to Mn ion dissolution. Thermodynamic values of solvation energy were calculated and related to the applied potential on the material during electrochemical cycling. Direct in situ observation of the degradation process was conducted on fiber structures using AFM and coin cell measurements, showing the rapid formation of theorized surface films. This provides the first direct evidence of processes occurring at the interface, such as dissolution of the active material, facet development, decomposition of the electrolyte to form a surface electrolyte interface (SEI) layer, or the