Ken-ichi Tonami

Resin–Dentin Bonding Interface After Photochemical Surface Treatment

OBJECTIVE The aim of this study is to elucidate the structure of the resin-dentin interface formed by photochemical dentin treatment using an argon fluoride (ArF) excimer laser. BACKGROUND DATA The ArF excimer laser processes material by photochemical reaction without generating heat, while also providing surface conditioning that enhances material adhesion. In the case of bonding between resin and dentin, we demonstrated in a previous study that laser etching using an ArF excimer laser produced bonding strength comparable to that of the traditional bonding process; however, conditions of the bonding interface have not been fully investigated. METHODS A dentin surface was irradiated in air with an ArF excimer laser followed by bonding treatment. Cross sections were observed under light microscope, transmission electron microscope (TEM), and scanning electron microscope, then analyzed using an energy dispersive X-ray spectroscope (EDS): EDS line profiles of the elements C, O, Si, Cl, P, and Ca at the resin-dentin interface were obtained. RESULTS The density of C in resin decreased as it approached the interface, reaching its lowest level within the dentin at a depth of 2 μm from the resin-dentin interface on EDS. There was no hybrid layer observed at the interface on TEM. Therefore, it was suggested that the resin monomer infiltrated into the microspaces produced on the dentin surface by laser abrasion. CONCLUSIONS The monomer infiltration without hybrid layer is thought to be the adhesion mechanism after laser etching. Therefore, the photochemical processes at the bonding interface achieved using the ArF excimer laser has great potential to be developed into a new bonding system in dentistry.

Effects of ArF Excimer Laser Irradiation of Dentin on the Tensile Bonding Strength to Composite Resin

OBJECTIVE The purpose of the study was to evaluate the effects of argon fluoride (ArF) excimer laser irradiation on the tensile bonding strength (TBS) of dentin to composite resin. BACKGROUND DATA Dental lasers use a photothermal process, which potentially entails risk of tissue damage caused by heat affecting the bond strength of resins. The ArF excimer laser functions by a photochemical process in which the energy of photons directly cuts covalent bonds in molecules without generating heat. METHODS Twenty extracted human molars were sectioned perpendicularly to the tooth axis to expose a flat dentin surface. The surfaces were treated with various combinations of ArF excimer laser irradiation, primer treatment, and bonding treatment. After composite resin was built up on the treated dentin surface, specimens with a 1×1 mm bonding interface were prepared and subjected to TBS tests. Treated dentin surfaces were also observed using transmission electron microscopy (TEM). RESULTS Specimens that underwent laser irradiation followed by bonding treatment had a TBS that did not differ significantly from that of specimens that received conventional treatment, with or without priming. TEM observations showed sectioned and dispersed collagen matrix in the hybrid layer after laser irradiation, priming, and bonding, but no hybrid layer after laser irradiation and bonding at the treated dentin surface. CONCLUSIONS The TBS of conditioning with ArF excimer laser irradiation was identical to that with conventional treatment when bonding was used. The bonding mechanism with the ArF irradiation differed from that of conventional bonding depending upon dentin hybridization.