Facile synthesis of very-long silver nanowires for transparent electrodes

Silver nanowires >60 μm and even 100 μm in length have been synthesized using a polyol process by adjusting the stirring speed at 130 °C. The length is over three times longer than that of normal AgNWs. These wires have a uniform ∼60 nm diameter, independent of the stirring speed. At 91% transmittance at 550 nm, AgNW films fabricated at room temperature achieved 25 Ω per square sheet resistance, which is superior to that of expensive ITO films.

The effect of light and humidity on the stability of silver nanowire transparent electrodes

Transparent electrodes based on silver nanowire (AgNW) films have attracted considerable attention owing to their high electrical and thermal conductivity, optical transparency, and flexibility. However, the long-term reliability of AgNW electrodes, has seldom been studied. In this work, the effects of storage environment, such as, natural light and humidity, on the long-term reliability have been investigated in detail. The increase of electrical resistance with storage time greatly depended on the natural light illumination, especially ultraviolet (UV) illumination, and high humidity seriously accelerated the failure of AgNW electrodes. All the results were dependent on the storage temperature. Some over-coating layers have been used to protect the AgNW electrodes from light and humidity in environment and the results showed that an epoxy resin protecting layer exhibited the longest lifetime: over 40 days at 85 °C and 85% relative humidity.