Sintering process investigation during polytetrafluoroethylene hollow fibre membrane fabrication by extrusion method

In this study, the effect of sintering conditions including manner, temperature and duration on properties of polytetrafluoroethylene (PTFE) hollow fibre membrane fabricated by extrusion method was intensively investigated. Different from un-sintered and relaxed sintered, the fixed sintered PTFE hollow fibre membrane was observed to generate a uniform ‘fibril–node’ porous structure and a main crystal transformation to folded chain crystal with smaller size. Consequently, it was found that for fixed setting sintering, both temperature increase from 340°C to 400°C and duration prolongation obviously improved pore size, ethanol permeation performance and mechanical strength. Additionally, the test results revealed that the membrane sintered below virgin melting point (350°C) had a noticeable higher porosity but poorer ethanol permeation performance that could be primarily attributed to increased ratio of closed pore. The sintering condition exhibited evident influence on PTFE hollow fibre membrane thermal stability, though it showed no alteration to the thermal decomposition of PTFE. The obtained PTFE hollow fibre membrane was tested to evaluate their vacuum membrane distillation (VMD) performances. It was found that PTFE membrane from lower sintering temperature delivered a better salt rejection; on the other hand, the permeate flux was improved by increased vacuum pressure during VMD operation.