On the formation of vertically oriented MCM-22 zeolite crystal films

Growth of MCM-22 zeolite films on glass substrates was studied with the focus on the understanding of the unusual vertical crystal orientation. The films formed were characterized by scanning electron microscopy and X-ray diffraction. Separate thin disk-like MCM-22 crystals were found vertically oriented at the early crystallization stage. With crystallization the crystals grew into thick disks and finally into continuous films. The vertically oriented MCM-22 thin crystals could be developed from the orientation of columnar MCM-22 nuclei, which have larger parameters in their c-directions than those in a and b directions. The preferred orientation of MCM-22 nuclei and the fast growth rate in the layer direction are responsible for the vertical growth of MCM-22 zeolite films.

Growth of ultrafine zeolite Y crystals on metakaolin microspheres

Ultrafine zeolite Y crystals (ca. 100–200 nm) have been successfully grown on metakaolin microspheres (<100 μm) for which good hydrothermal stability was observed; products were characterized by powder X-ray diffraction, scanning electronic microscopy and transmission electronic microscopy.

Oriented growth of MCM-22 zeolite films

MCM-22 zeolite films have been grown with layers vertical to the substrate under hydrothermal synthesis conditions, and characterized by X-ray diffraction and scanning electron microscopy.