Effect of ZnO on the Physical Properties and Optical Band Gap of Soda Lime Silicate Glass

This manuscript reports on the physical properties and optical band gap of five samples of soda lime silicate (SLS) glass combined with zinc oxide (ZnO) that were prepared by a melting and quenching process. To understand the role of ZnO in this glass structure, the density, molar volume and optical band gaps were investigated. The density and absorption spectra in the Ultra-Violet-Visible (UV-Visible) region were recorded at room temperature. The results show that the densities of the glass samples increased as the ZnO weight percentage increased. The molar volume of the glasses shows the same trend as the density: the molar volume increased as the ZnO content increased. The optical band gaps were calculated from the absorption edge, and it was found that the optical band gap decreased from 3.20 to 2.32 eV as the ZnO concentration increased.

Effect of Low Concentration Sn Doping on Optical Properties of CdS Films Grown by CBD Technique

Thin and transparent films of doped cadmium sulfide (CdS) were obtained on commercial glass substrates by Chemical Bath Deposition (CBD) technique. The films were doped with low concentration of Sn, and annealed in air at 300 °C for 45 min. The morphological characterization of the films with different amounts of dopant was made using SEM and EDAX analysis. Optical properties of the films were evaluated by measuring transmittance using the UV-vis spectrophotometer. A comparison of the results revealed that lower concentration of Sn doping improves transmittance of CdS films and makes them suitable for application as window layer of CdTe/CIGS solar cells.

Studying the Effect of ZnO on Physical and Elastic Properties of (ZnO)x(P2O5)1−x Glasses Using Nondestructive Ultrasonic Method

Binary zinc phosphate glass system with composition of (ZnO)x(P2O5)1−x, ( = 0.1, 0.2, 0.3, 0.4, 0.5 and 0.6 mol%) was successfully prepared using a conventional melt-quenching method. Composition dependence of physical properties and elastic properties in the (ZnO)x(P2O5)1−x were discussed in association with the effects of adding zinc oxide (ZnO) as a modifier. The addition of ZnO modifier was expected to produce substantial changes on physical properties of the phosphate glasses. An increase in density values of the phosphate glasses was observed. Elastic moduli were studied by measuring ultrasonic longitudinal and shear velocities ( and ) of the glasses at room. Longitudinal modulus, shear modulus, bulk modulus, Young’s modulus, Poisson’s ratio, and Debye temperature were derived from both data of velocities and respective density of all of the samples. Findings from present work showed dependence of density and elastic moduli of each ZnO-P2O5 series on glass composition.

Synthesis mechanism of low-voltage praseodymium oxide doped zinc oxide varistor ceramics prepared through modified citrate gel coating.

High demands on low-voltage electronics have increased the need for zinc oxide (ZnO) varistors with fast response, highly non-linear current-voltage characteristics and energy absorption capabilities at low breakdown voltage. However, trade-off between breakdown voltage and grain size poses a critical bottle-neck in the production of low-voltage varistors. The present study highlights the synthesis mechanism for obtaining praseodymium oxide (Pr6O11) based ZnO varistor ceramics having breakdown voltages of 2.8 to 13.3 V/mm through employment of direct modified citrate gel coating technique. Precursor powder and its ceramics were examined by means of TG/DTG, FTIR, XRD and FESEM analyses. The electrical properties as a function of Pr6O11 addition were analyzed on the basis of I-V characteristic measurement. The breakdown voltage could be adjusted from 0.01 to 0.06 V per grain boundary by controlling the amount of Pr6O11 from 0.2 to 0.8 mol%, without alteration of the grain size. The non-linearity coefficient, α, varied from 3.0 to 3.5 and the barrier height ranged from 0.56 to 0.64 eV. Breakdown voltage and α lowering with increasing Pr6O11 content were associated to reduction in the barrier height caused by variation in O vacancies at grain boundary.

Effect of Annealing Temperature on the Optical Spectra of CdS Thin Films Deposited at Low Solution Concentrations by Chemical Bath Deposition (CBD) Technique

Two different concentrations of CdCl2 and (NH2)2CS were used to prepare CdS thin films, to be deposited on glass substrate by chemical bath deposition (CBD) technique. CdCl2 (0.000312 M and 0.000625 M) was employed as a source of Cd2+ while (NH2)2CS (0.00125 M and 0.000625 M) for S2− at a constant bath temperature of 70 °C. Adhesion of the deposited films was found to be very good for all the solution concentrations of both reagents. The films were air-annealed at a temperature between 200 °C to 360 °C for one hour. The minimum thickness was observed to be 33.6 nm for film annealed at 320 °C. XRD analyses reveal that the films were cubic along with peaks of hexagonal phase for all film samples. The crystallite size of the films decreased from 41.4 nm to 7.4 nm with the increase of annealing temperature for the CdCl2 (0.000312 M). Optical energy band gap (Eg), Urbach energy (Eu) and absorption coefficient (α) have been calculated from the transmission spectral data. These parameters have been discussed as a function of annealing temperature and solution concentration. The best transmission (about 97%) was obtained for the air-annealed films at higher temperature at CdCl2 (0.000312 M).

Photopyroelectric Spectroscopic Studies of ZnO-MnO2-Co3O4-V2O5 Ceramics

Photopyroelectric (PPE) spectroscopy is a nondestructive tool that is used to study the optical properties of the ceramics (ZnO + 0.4MnO2 + 0.4Co3O4 + xV2O5), x = 0–1 mol%. Wavelength of incident light, modulated at 10 Hz, was in the range of 300–800 nm. PPE spectrum with reference to the doping level and sintering temperature is discussed. Optical energy band-gap (Eg) was 2.11 eV for 0.3 mol% V2O5 at a sintering temperature of 1025 °C as determined from the plot (ρhυ)2 versus hυ. With a further increase in V2O5, the value of Eg was found to be 2.59 eV. Steepness factor ‘σA’ and ‘σB’, which characterize the slope of exponential optical absorption, is discussed with reference to the variation of Eg. XRD, SEM and EDAX are also used for characterization of the ceramic. For this ceramic, the maximum relative density and grain size was observed to be 91.8% and 9.5 μm, respectively.

Use of a Reflectance Spectroscopy Accessory for Optical Characterization of ZnO-Bi2O3-TiO2 Ceramics

The optical band-gap energy (Eg) is an important feature of semiconductors which determines their applications in optoelectronics. Therefore, it is necessary to investigate the electronic states of ceramic ZnO and the effect of doped impurities under different processing conditions. Eg of the ceramic ZnO + xBi2O3 + xTiO2, where x = 0.5 mol%, was determined using a UV-Vis spectrophotometer attached to a Reflectance Spectroscopy Accessory for powdered samples. The samples was prepared using the solid-state route and sintered at temperatures from 1140 to 1260 °C for 45 and 90 minutes. Eg was observed to decrease with an increase of sintering temperature. XRD analysis indicated hexagonal ZnO and few small peaks of intergranular layers of secondary phases. The relative density of the sintered ceramics decreased and the average grain size increased with the increase of sintering temperature.

Green Synthesis and Characterization of Hydroxyapatite from Fish Scale Biowaste

The present study was undertaken to study the effect of calcinate temperature on characteristics of hydroxyapatite synthesized from the fish scale (FHAp). The FHAp calcined at different temperatures starting from 100 up to 300 °C. The structures of FHAP were characterized by Fourier transform infrared spectroscopy, scanning electron microscopy, and X-ray diffraction. The analytical results show that the FHAp quality increased as the calcin temperature increased. The FHAp displayed excellent characteristics in term of particle size, morphology and properties and crystalinity after calcined at 300 °C, FHAp 300. From this study, it founded that 300 °C is the lowest calcin temperature could be applied to synthesize high quality of HAp from fish scale biowaste.

Characterization of CdTe Films Deposited at Various Bath Temperatures and Concentrations Using Electrophoretic Deposition

CdTe film was deposited using the electrophoretic deposition technique onto an ITO glass at various bath temperatures. Four batch film compositions were used by mixing 1 to 4 wt% concentration of CdTe powder with 10 mL of a solution of methanol and toluene. X-ray Diffraction analysis showed that the films exhibited polycrystalline nature of zinc-blende structure with the (111) orientation as the most prominent peak. From the Atomic Force Microscopy, the thickness and surface roughness of the CdTe film increased with the increase of CdTe concentration. The optical energy band gap of film decreased with the increase of CdTe concentration, and with the increase of isothermal bath temperature. The film thickness increased with respect to the increase of CdTe concentration and bath temperature, and following, the numerical expression for the film thickness with respect to these two variables has been established.

Scan rate effect of titania for hybrid solar cell applications: Structural and electrical study

The AIP In this research, hybrid solar cell are produce by a combination of organic (Areca Catechu) extraction and Poly (3-hexylthiophene) (P3HT) and inorganic Titanium Dioxide, TiO2 materials. These hybrid solar cells are fabricated accordingly by layered of ITO/TiO2/P3HT/Areca Catechu/Au by using electrochemical method. The deposition of each layered by EIS was different by varied the scan rate of TiO2 deposition which are 0.05, 0.07, 0.09 and 0.11 vs-1 whereas the number of scans of each layers are fixed to 5 numbers of scans. Nanocrystals TiO2 (anatase structured) was prepared by dissolving the TiO2 nanoparticles with acetic acid which acts as capping agent in order to gain TiO2 nanostructures with better-controlled size and shape. Field Emission Scanning Electron Microscope (FESEM) images indicates that the TiO2 nanoparticles size was found to be around 15-34 nm. The XRD patterns indicate that the TiO2 film was highly crystalline and the anatase structure of TiO2 remains unchanged after annealed proc...