Nakashima Hideharu

Instantaneous creep in face-centered cubic metals at ultralow strain rates by a high-resolution strain measurement

Instantaneous creep in face-centered cubic metals, 5N Al (99.999%), 2N Al (99%) and 4N Cu (99.99%) with different grain sizes, was firstly investigated by sudden stress-change experiments at ultralow strain rates

一軸引張試験による低炭素焼き入れ,及び分割化鋼中の残留オーステナイトの変形挙動のその場EBSD研究【Powered by NICT】

\dot \varepsilon

部分と完全オーステナイト化後のミクロ組織の発達と低炭素焼き入れ,及び分割化鋼の機械的性質【Powered by NICT】

⩽ 10−10 s−1 and temperature T < 0.32 Tm. The experimental results indicate that the observed instantaneous creep is strongly dependent on grain size, the concentration of impurity, and stacking fault energy. Creep in high-purity aluminum, 5N Al, with a very large grain size, dg > 1600 μm, shows non-viscous behavior, and is controlled by the recovery of dislocations in the boundary of dislocation cells. On the other hand, for 5N Al with a small grain size, dg=30 μm, and low-purity aluminum, 2N Al, with dg= 25 μm, creep shows viscous behavior and may be related to ‘low temperature grain boundary sliding’. For high-purity copper, 4N Cu, with dg= 40 μm and lower stacking fault energy, creep shows a non-viscous behavior, and is controlled by the recovery process of dislocations. For all of the samples, creep shows anelastic behavior.