Rafael Massunari Maenosono

Influence of Volume and Activation Mode on Polymerization Shrinkage Forces of Resin Cements

The concern with the polymerization shrinkage of restorative resin composites also applies to resin cements. The aim of this study was to evaluate the influence of volume and polymerization mode on forces generated during polymerization shrinkage (FGPS) of resin cements. Two light-cured resin cements--Variolink II (VL; Ivoclar Vivadent) and Nexus 3 (NX; Kerr)--and two self-cured resin cements - Multilink (ML; Ivoclar Vivadent) and Cement Post (CP; Angelus) - were inserted between two rectangular steel bases (6x2 mm) with distance set at 0.1, 0.3 and 0.5 mm, establishing a variation of volume. These steel bases were attached to a universal test machine with 50 kg load cell and forces (N) were registered for 10 min. Values of maximum forces generated by each material were subjected to two-way ANOVA and Tukeys test for individual comparisons (α=0.05). VL, NX and CP developed increasing FGPS as the volume of material increased, while ML presented the opposite behavior. It may be concluded that higher volume increases FGPS even with a concomitant decrease of C-factor, unless the resin cements present lower force generation rates as a function of time in combination with a low C-factor, resulting in stress relief and consequently lower values of FGPS.

Water interaction and bond strength to dentin of dye-labelled adhesive as a function of the addition of rhodamine B

ABSTRACT Objective This study investigated the effect of the fluorescent dye rhodamine B (RB) for interfacial micromorphology analysis of dental composite restorations on water sorption/solubility (WS/WSL) and microtensile bond strength to dentin (µTBS) of a 3-step total etch and a 2-step self-etch adhesive system. Material and Methods The adhesives Adper Scotchbond Multi-Purpose (MP) and Clearfil SE Bond (SE) were mixed with 0.1 mg/mL of RB. For the WS/WSL tests, cured resin disks (5.0 mm in diameter x 0.8 mm thick) were prepared and assigned into four groups (n=10): MP, MP-RB, SE, and SE-RB. For µTBS assessment, extracted human third molars (n=40) had the flat occlusal dentin prepared and assigned into the same experimental groups (n=10). After the bonding and restoration procedures, specimens were sectioned in rectangular beams, stored in water and tested after seven days or after 12 months. The failure mode of fractured specimens was qualitatively evaluated under optical microscope (x40). Data from WS/WSL and µTBS were assessed by one-way and three-way ANOVA, respectively, and Tukey’s test (α=5%). Results RB increased the WSL of MP and SE. On the other hand, WS of both MP and SE was not affected by the addition of RB. No significance in µTBS between MP and MP-RB for seven days or one year was observed, whereas for SE a decrease in the µTBS means occurred in both storage times. Conclusions RB should be incorporated into non-simplified DBSs with caution, as it can interfere with their physical-mechanical properties, leading to a possible misinterpretation of bonded interface.

In Vitro Evaluation of Dentin Hydraulic Conductance After 980 nm Diode Laser Irradiation

BACKGROUND Dentin hypersensitivity treatments are based on the physical obliteration of the dentinal tubules to reduce hydraulic conductance. The aim of the present study is to evaluate the hydraulic conductance of bovine root dentin after irradiation with a 980-nm diode laser, with or without associated fluoride varnish. METHODS Sixty bovine root dentin specimens were divided into six groups (n = 10 in each group): G1, G3, and G5 (0.5 W, 0.7 W, and 1 W diode laser, respectively); G2, G4, and G6 (fluoride varnish application + 0.5 W, 0.7 W, and 1 W diode laser, respectively). The dentin hydraulic conductance was evaluated at four time periods with a fluxmeter: 1) with smear layer, 2) after 37% phosphoric acid etching, 3) after the treatments, and 4) after 6% citric acid challenge. After the dentinal fluid flow measurements, specimens were also evaluated for mineral composition using energy dispersive X-ray spectroscopy (EDS). RESULTS Analysis demonstrated a better result with increased irradiation power (P < 0.001), especially if the diode laser irradiation was associated with the application of fluoride varnish (P < 0.001), ensuring a greater reduction in permeability. Considering the groups treated only with laser irradiation, the 1 W group was superior when compared with the 0.5 W and 0.7 W irradiated groups immediately after treatment (P < 0.001). After citric acid testing, all groups showed similar results, except when comparing the 1 W groups with the 0.5 W groups (P = 0.04). EDS results of the irradiated groups showed an increase in the proportion of calcium and phosphorus ions, which demonstrates a superficial composition modification after laser treatments. CONCLUSION Laser irradiation of exposed dentin promoted significant reduction in the dentin hydraulic conductance, mainly with higher energy densities and association with fluoride varnish.

Does laser diode irradiation improve the degree of conversion of simplified dentin bonding systems

Abstract Simplified dentin-bonding systems are clinically employed for most adhesive procedures, and they are prone to hydrolytic degradation. Objective This study aimed to investigate the effect of laser diode irradiation on the degree of conversion (DC), water sorption (WS), and water solubility (WSB) of these bonding systems in an attempt to improve their physico-mechanical resistance. Material and Methods Two bonding agents were tested: a two-step total-etch system [Adper™ Single Bond 2, 3M ESPE (SB)] and a universal system [Adper™ Single Bond Universal, 3M ESPE (SU)]. Square-shaped specimens were prepared and assigned into 4 groups (n=5): SB and SU (control groups – no laser irradiation) and SB-L and SU-L [SB and SU laser (L) – irradiated groups]. DC was assessed using Fourier transform infrared spectroscopy with attenuated total reflectance. Additional uncured resin samples (≈3.0 µL, n=5) of each adhesive were also scanned for final DC calculation. For WS/WSB tests, similar specimens (n=10) were prepared and measured by monitoring the mass changes after dehydration/water storage cycles. For both tests, adhesive fluids were dropped into standardized Teflon molds (6.0×6.0×1.0 mm), irradiated with a 970-nm laser diode, and then polymerized with an LED-curing unit (1 W/cm2). Results Laser irradiation immediately before photopolymerization increased the DC (%) of the tested adhesives: SB-L>SB>SU-L>SU. For WS/WSB (μg/mm3), only the dentin bonding system (DBS) was a significant factor (p<0.05): SB>SU. Conclusion Irradiation with a laser diode improved the degree of conversion of all tested simplified dentin bonding systems, with no impact on water sorption and solubility.

Effect of Two Antioxidants Agents on Microtensile Bond Strength to Bleached Enamel

This in vitro study evaluated the effect of sodium bicarbonate and sodium ascorbate on the microtensile bond strength of an etch-and-rinse system to bleached bovine enamel. Sixty bovine enamel blocks (4x4 mm) were flattened and randomly allocated into 5 groups: G1 (negative control): without treatment; G2 (positive control): bleached with 35% hydrogen peroxide (HP); G3: bleached and stored for 7 days in artificial saliva before restorative procedures; G4: bleached and treated with 10% sodium bicarbonate solution for 5 min; G5: bleached and treated with 10% sodium ascorbate hydrogel for 15 min. HP gel was applied twice (20 min each, except in G1) and the adhesive restorations were performed. After 24 h, the specimens were sectioned into sticks and submitted to microtensile bond strength testing with a crosshead speed of 0.5 mm/min (n=12). As a complementary visual observation, the enamel surfaces of the G1 and G2 specimens were evaluated with scanning electron microscopy. Data were analyzed by one-way ANOVA (p<0.05). The means (standard deviation) were: G1: 24.22±7.74; G2: 18.29±5.88; G3: 40.88±7.95; G4: 19.95±5.67 and G5: 24.43±6.43. Adhesive failures were predominant in all groups. The comparison between the treatments indicates that waiting 7 days after bleaching is still the most effective approach. When this waiting period is not possible, application of sodium ascorbate or sodium bicarbonate seems to be a good alternative. Therefore, the practicality of obtaining sodium bicarbonate in the bleaching kits and its higher stability enables its clinical use.