Journal of Applied Oral Science | 2009
Rafael Francisco Lia Mondelli; Sérgio Kiyoshi Ishikiriama; Otávio de Oliveira Filho; José Mondelli
Objectives: This in vitro study evaluated the fracture resistance of weakened human premolars (MOD cavity preparation and pulp chamber roof removal) restored with condensable resin composite with and without cusp coverage. Material and Methods: Thirty human maxillary premolars were divided into three groups: Group A (control), sound teeth; Group B, wide MOD cavities prepared and the pulp chamber roof removed and restored with resin composite without cusp coverage; Group C, same as Group B with 2.0 mm of buccal and palatal cusps reduced and restored with the same resin. The teeth were included in metal rings with self-curing acrylic resin, stored in water for 24 h and thereafter subjected to a compressive axial load in a universal testing machine at 0.5 mm/min. Results: The mean fracture resistance values ± standart deviation (kgf) were: group A: 151.40 ± 55.32, group B: 60.54 ± 12.61, group C: 141.90 ± 30.82. Statistically significant differences were found only between Group B and the other groups (p<0.05). The condensable resin restoration of weakened human premolars with cusp coverage significantly increased the fracture resistance of the teeth as compared to teeth restored without cusp coverage. Conclusion: The results showed that cusp coverage with condensable resin might be a safe option for restoring weakened endodontically treated teeth.
Journal of Applied Oral Science | 2012
Gabriela Ulian de Oliveira; Rafael Francisco Lia Mondelli; Marcela C. Rodrigues; Eduardo Batista Franco; Sérgio Kiyoshi Ishikiriama; Linda Wang
Objectives Nanofilled composite resins are claimed to provide superior mechanical properties compared with microhybrid resins. Thus, the aim of this study was to compare nanofilled with microhybrid composite resins. The null hypothesis was that the size and the distribution of fillers do not influence the mechanical properties of surface roughness and wear after simulated toothbrushing test. Material and methods Ten rectangular specimens (15 mm x 5 mm x 4 mm) of Filtek Z250 (FZ2), Admira (A), TPH3 (T),Esthet-X (EX), Estelite Sigma (ES), Concept Advanced (C), Grandio (G) and Filtek Z350 (F) were prepared according to manufacturers instructions. Half of each top surface was protected with nail polish as control surface (not brushed) while the other half was assessed with five random readings using a roughness tester (Ra). Following, the specimens were abraded by simulated toothbrushing with soft toothbrushes and slurry comprised of 2:1 water and dentifrice (w/w). 100,000 strokes were performed and the brushed surfaces were re-analyzed. Nail polish layers were removed from the specimens so that the roughness (Ra) and the wear could be assessed with three random readings (µm). Data were analyzed by ANOVA and Tukeys multiple-comparison test (α=0.05). Results Overall outcomes indicated that composite resins showed a significant increase in roughness after simulated toothbrushing, except for Grandio, which presented a smoother surface. Generally, wear of nanofilled resins was significantly lower compared with microhybrid resins. Conclusions As restorative materials suffer alterations under mechanical challenges, such as toothbrushing, the use of nanofilled materials seem to be more resistant than microhybrid composite resins, being less prone to be rougher and worn.
Brazilian Dental Journal | 2013
Sérgio Kiyoshi Ishikiriama; Rafael Massunari Maenosono; Denise Ferracioli Oda; Juan Fernando Ordoñéz-Aguilera; Linda Wang; Rafael Francisco Lia Mondelli
The concern with the polymerization shrinkage of restorative resin composites also applies to resin cements. The aim of this study was to evaluate the influence of volume and polymerization mode on forces generated during polymerization shrinkage (FGPS) of resin cements. Two light-cured resin cements--Variolink II (VL; Ivoclar Vivadent) and Nexus 3 (NX; Kerr)--and two self-cured resin cements - Multilink (ML; Ivoclar Vivadent) and Cement Post (CP; Angelus) - were inserted between two rectangular steel bases (6x2 mm) with distance set at 0.1, 0.3 and 0.5 mm, establishing a variation of volume. These steel bases were attached to a universal test machine with 50 kg load cell and forces (N) were registered for 10 min. Values of maximum forces generated by each material were subjected to two-way ANOVA and Tukeys test for individual comparisons (α=0.05). VL, NX and CP developed increasing FGPS as the volume of material increased, while ML presented the opposite behavior. It may be concluded that higher volume increases FGPS even with a concomitant decrease of C-factor, unless the resin cements present lower force generation rates as a function of time in combination with a low C-factor, resulting in stress relief and consequently lower values of FGPS.
Journal of Dentistry | 2014
Diana Ferreira Gadelha de Araújo; Larissa Pinceli Chaves; Odair Bim Júnior; Fernanda Cristina Pimentel Garcia; Sérgio Kiyoshi Ishikiriama; Heitor Marques Honório; Linda Wang
OBJECTIVES This study evaluated the influence of 2% chlorhexidine digluconate (CHX) on the bond strength (BS) of a glass-fibre post to the root canal, regarding the cements (dual-cured resin or resin-modified glass-ionomer cement), the root thirds and the time of storage. METHOD Eighty bovine roots were selected and endodontically treated, before being randomly assigned to the following groups according to the luting protocol: ARC (RelyX ARC); ARC+CHX; RL (RelyX Luting 2); and RL+CHX. After 24 h of luting, the roots were sliced to obtain 1 mm-thick slices. Half of each group was submitted to either 7-day or 6-month storage in artificial saliva (n=10). The specimens were subjected to push-out tests with a crosshead speed of 0.5 mm/min. The data were analysed with four-way ANOVA and Tukeys test (P≤0.05). The failure modes were analysed with a digital microscope (50× and 200×). RESULTS ARC yielded a significantly higher BS compared to RL (P<0.001). Despite CHX exerted a significant effect; it depends on the interaction with the luting cement and time (P<0.001). Thus, CHX decreased the values of BS to those of ARC after 6 months (P<0.001). On the 7th day of storage, the ARC+CHX presented higher BS to the cervical and middle thirds compared to RL+CHX (P=0.012). Time solely was not a significant factor (P=0.081). Adhesive cement-dentine type and mixed failures were predominant modes for the ARC groups. For the RL groups, the main failures were adhesive cement-post and mixed modes. CONCLUSIONS Glass-fibre posts luted with RelyX ARC dual-cure resin cement exhibited higher BS than those luted with RelyX Luting 2 resin-modified glass-ionomer cement. Furthermore, CHX was not effective to improve the BS and negatively affected the BS of RelyX ARC after 6 months of storage. CLINICAL SIGNIFICANCE The use of chlorhexidine solution seems not to improve the bond strength of fibre posts to root canals, disregarding the composition of the luting cement.
Angle Orthodontist | 2012
Daniela Gamba Garib; Guilherme Janson; Patrícia Bittencourt Dutra dos Santos; Taiana de Oliveira Baldo; Gabriela Ulian de Oliveira; Sérgio Kiyoshi Ishikiriama
Orthodontic space closure is a treatment alternative when a maxillary central incisor is missing. The objective of this report was to present an unusual treatment in which a right maxillary central incisor was moved through the midpalatal suture to replace the absent contralateral tooth. The biologic aspects and clinical appearance of the recontoured lateral and central incisors were analyzed. The position of the examined teeth and the appearance of the surrounding soft tissues were satisfactory; however, the upper midline frenulum deviated to the left. The incisor was successfully moved with no obvious detrimental effects as observed on the final radiographs. In the radiographic and tomographic examinations, the midline suture seemed to have followed the tooth movement. The patient expressed satisfaction with the results. It was concluded that orthodontic movement of the central incisor to replace a missing contralateral tooth is a valid treatment option, and the achievement of an esthetic result requires an interdisciplinary approach, including restorative dentistry and periodontics.
Journal of Periodontology | 2016
Fabio Antonio Piola Rizzante; Rafael Massunari Maenosono; Marco Antonio Hungaro Duarte; Adilson Yoshio Furuse; Regina Guenka Palma-Dibb; Sérgio Kiyoshi Ishikiriama
BACKGROUND Dentin hypersensitivity treatments are based on the physical obliteration of the dentinal tubules to reduce hydraulic conductance. The aim of the present study is to evaluate the hydraulic conductance of bovine root dentin after irradiation with a 980-nm diode laser, with or without associated fluoride varnish. METHODS Sixty bovine root dentin specimens were divided into six groups (n = 10 in each group): G1, G3, and G5 (0.5 W, 0.7 W, and 1 W diode laser, respectively); G2, G4, and G6 (fluoride varnish application + 0.5 W, 0.7 W, and 1 W diode laser, respectively). The dentin hydraulic conductance was evaluated at four time periods with a fluxmeter: 1) with smear layer, 2) after 37% phosphoric acid etching, 3) after the treatments, and 4) after 6% citric acid challenge. After the dentinal fluid flow measurements, specimens were also evaluated for mineral composition using energy dispersive X-ray spectroscopy (EDS). RESULTS Analysis demonstrated a better result with increased irradiation power (P < 0.001), especially if the diode laser irradiation was associated with the application of fluoride varnish (P < 0.001), ensuring a greater reduction in permeability. Considering the groups treated only with laser irradiation, the 1 W group was superior when compared with the 0.5 W and 0.7 W irradiated groups immediately after treatment (P < 0.001). After citric acid testing, all groups showed similar results, except when comparing the 1 W groups with the 0.5 W groups (P = 0.04). EDS results of the irradiated groups showed an increase in the proportion of calcium and phosphorus ions, which demonstrates a superficial composition modification after laser treatments. CONCLUSION Laser irradiation of exposed dentin promoted significant reduction in the dentin hydraulic conductance, mainly with higher energy densities and association with fluoride varnish.
Brazilian Oral Research | 2015
Camila Moreira Machado; Aline Cristina Zamuner; Karin Cristina da Silva Modena; Sérgio Kiyoshi Ishikiriama; Linda Wang
Concern has been raised about the bonding of restorative procedures to an erosive lesion, given the change in organic and inorganic composition and structure of this substrate. This in vitro study evaluated the effect of erosive drinks and an enzyme inhibitor (2% chlorhexidine digluconate - 2% CHX) on bond strength to dentin. Sixty sound human third molars were selected, and the occlusal enamel was flattened, exposing the dentin surface. The specimens were randomly divided into three groups: AS-Artificial saliva (control group), RC- Regular Cola and ZC- Zero Cola. Twenty specimens were immersed in their respective solution for 1 minute, 3 times a day, over the course of 5 days. After acid etching and before bonding with Adper Single Bond 2, half of the samples of each group (n = 10) were treated with 2% CHX, whereas the other half (n = 10) were not, forming the control group (CONV). All the specimens were restored with Filtek Z250 composite resin filled in Tygon tubes (0.48 mm2), yielding six microcylinders for microshear bond strength testing. Three composite resin microcylinders of each specimen were tested after 1 month, and the remaining microcylinders were tested after 6 months. Failure modes were determined using a stereomicroscope (40x). The data were statistically analyzed by three-way ANOVA and Tukey tests (α = 0.05). Overall bonding was reduced after 6 months, regardless of treatment. The 2% CHX enhanced bond strength after 1 month only in the ZC group, and did not enhance bonding performance to demineralized dentin by erosive protocol after 6 months in any group.
Journal of Applied Oral Science | 2016
Rafael Francisco Lia Mondelli; Ana Flávia Soares; Eugenio Kegler Pangrazio; Linda Wang; Sérgio Kiyoshi Ishikiriama; Juliana Fraga Soares Bombonatti
ABSTRACT The use of light sources in the bleaching process reduces the time required and promotes satisfactory results. However, these light sources can cause an increase in the pulp temperature. Objective The purpose of the present study was to measure the increase in intrapulpal temperature induced by different light-activated bleaching procedures with and without the use of a bleaching gel. Material and Methods A human maxillary central incisor was sectioned 2 mm below the cementoenamel junction. A K-type thermocouple probe was introduced into the pulp chamber. A 35% hydrogen peroxide bleaching gel was applied to the vestibular tooth surface. The light units used were a conventional halogen, a hybrid light (only LED and LED/Laser), a high intensity LED, and a green LED light. Temperature increase values were compared by two-way ANOVA and Tukey´s tests (p<0.05). Results There were statistically significant differences in temperature increases between the different light sources used and between the same light sources with and without the use of a bleaching gel. The presence of a bleaching gel generated an increase in intra-pulpal temperature in groups activated with halogen light, hybrid light, and high intensity LED. Compared to the other light sources, the conventional halogen lamp applied over the bleaching gel induced a significant increase in temperature (3.83±0.41°C). The green LED unit with and without gel application did not produce any significant intrapulpal temperature variations. Conclusion In the present study, the conventional halogen lamp caused the highest increase in intrapulpal temperature, and the green LED caused the least. There was an increase in temperature with all lights tested and the maximum temperature remained below the critical level (5.5°C). The addition of a bleaching gel led to a higher increase in intrapulpal temperatures.
Journal of The Mechanical Behavior of Biomedical Materials | 2018
Fabio Antonio Piola Rizzante; Paula Minatel Locatelli; Thiago Soares Porto; Ana Flávia Sanches Borges; Rafael Francisco Lia Mondelli; Sérgio Kiyoshi Ishikiriama
The purpose of this in vitro study was to compare the micro hardness, color stability/ΔE, and degree of conversion/DC of a resin cement light cured through different ceramic spacers. Lithium-disilicate ceramic samples were obtained from IPS E-max CAD blocks (HT A1) and IPS in-Ceram (transparent neutral); and divided in 7 groups (n = 8 for each test): CTR/control group; 06 M/0.6 mm monolithic; 12 M/1.2 mm monolithic; 20 M/2.0 mm monolithic; 06B/0.4 + 0.2 mm bilayered; 12B/1.0 + 0.2 mm bilayered; 20B/1.8 + 0.2 mm bilayered. The resin cement (Variolink veneer) was light cured through the ceramic spacers. The resin cement samples were evaluated for ΔE using a spectrophotometer after 24 h, 7days and after aging (24 h in water at 60 °C). Knoop microhardness and DC tests were conducted immediately after light curing, after 24 h and 7days. All experimental groups showed similar microhardness values, although being lower than CTR group. Similar results were observed after 7days. ΔE was similar between all groups after 24 h (except for 12B and 20B), and increased for all groups after 7days and after artificial aging, especially for thicker and bilayer groups. Only 06 M showed values similar to CTR group. DC values were similar to all groups immediately after light curing, increasing after 24 h and 7days. After 7days, only group 20B showed lower DC than CTR group. A tendency of higher DC could be observed for monolithic and thinner ceramics. All test results showed strong correlation (0.9987). Ceramic interposition can reduce mechanical and physical properties of resin cements, especially with thicker and bilayered ceramics. Group 06 M showed the best ΔE overtime.
Journal of Applied Oral Science | 2017
Letícia Ferreira de Freitas Brianezzi; Rafael Massunari Maenosono; Odair Bim Júnior; Giovanna Speranza Zabeu; Regina Guenka Palma-Dibb; Sérgio Kiyoshi Ishikiriama
Abstract Simplified dentin-bonding systems are clinically employed for most adhesive procedures, and they are prone to hydrolytic degradation. Objective This study aimed to investigate the effect of laser diode irradiation on the degree of conversion (DC), water sorption (WS), and water solubility (WSB) of these bonding systems in an attempt to improve their physico-mechanical resistance. Material and Methods Two bonding agents were tested: a two-step total-etch system [Adper™ Single Bond 2, 3M ESPE (SB)] and a universal system [Adper™ Single Bond Universal, 3M ESPE (SU)]. Square-shaped specimens were prepared and assigned into 4 groups (n=5): SB and SU (control groups – no laser irradiation) and SB-L and SU-L [SB and SU laser (L) – irradiated groups]. DC was assessed using Fourier transform infrared spectroscopy with attenuated total reflectance. Additional uncured resin samples (≈3.0 µL, n=5) of each adhesive were also scanned for final DC calculation. For WS/WSB tests, similar specimens (n=10) were prepared and measured by monitoring the mass changes after dehydration/water storage cycles. For both tests, adhesive fluids were dropped into standardized Teflon molds (6.0×6.0×1.0 mm), irradiated with a 970-nm laser diode, and then polymerized with an LED-curing unit (1 W/cm2). Results Laser irradiation immediately before photopolymerization increased the DC (%) of the tested adhesives: SB-L>SB>SU-L>SU. For WS/WSB (μg/mm3), only the dentin bonding system (DBS) was a significant factor (p<0.05): SB>SU. Conclusion Irradiation with a laser diode improved the degree of conversion of all tested simplified dentin bonding systems, with no impact on water sorption and solubility.