Zeolite templated carbon materials for high pressure hydrogen storage

Zeolite-templated carbon (ZTC) materials were synthesized, characterized, and evaluated as potential hydrogen storage materials between 77 and 298 K up to 30 MPa. Successful synthesis of high template fidelity ZTCs was confirmed by X-ray diffraction and nitrogen adsorption at 77 K; BET surface areas up to ~3600 m(2) g(-1) were achieved. Equilibrium hydrogen adsorption capacity in ZTCs is higher than all other materials studied, including superactivated carbon MSC-30. The ZTCs showed a maximum in Gibbs surface excess uptake of 28.6 mmol g(-1) (5.5 wt %) at 77 K, with hydrogen uptake capacity at 300 K linearly proportional to BET surface area: 2.3 mmol g(-1) (0.46 wt %) uptake per 1000 m(2) g(-1) at 30 MPa. This is the same trend as for other carbonaceous materials, implying that the nature of high-pressure adsorption in ZTCs is not unique despite their narrow microporosity and significantly lower skeletal densities. Isoexcess enthalpies of adsorption are calculated between 77 and 298 K and found to be 6.5-6.6 kJ mol(-1) in the Henrys law limit.