Formation of Transition Metal Cluster Adducts on the Surface of Single-walled Carbon Nanotubes: HRTEM Studies

We report the formation of chromium clusters on the outer walls of single-walled carbon nanotubes (SWNTs). The clusters were obtained by reacting purified SWNTs with chromium hexacarbonyl in dibutyl ether at 100°C. The functionalized SWNTs were characterized by thermogravimetic analysis, XPS, and high-resolution TEM. The curvature of the SWNTs and the high mobility of the chromium moieties on graphitic surfaces allow the growth of the metal clusters and we propose a mechanism for their formation.

Synthesis and characterisation of amorphous SeTe nanorods prepared by ball milling

The amorphous Se97Te3 nanorods were prepared by mechanical milling. The amorphous Se97Te3 materials were used as a starting material. The milled materials were characterisation by XRD, TEM and optical measurement by JASCO, UV/VIS/NIR spectrophotometer in a wavelength region 300 nm-1000 nm. The experimental result shows that an amorphous stage is also achieved during the milling process. TEM analysis showed that after 50 hours of milling time, multi-walled amorphous nanorods were formed with a diameter of about 90 nm and after 60 hours of milling time amorphous nanowires of about 80 nm diameter was formed. The optical absorption measurement indicates that the absorption mechanism is due to indirect transition. It has been observed that the absorption coefficient increases lineally with the increase in photon energy and the optical band gap increases with the increase of milling time.