Sharizal Hasan

Role of CA-EDTA on the Synthesizing Process of Cerate-Zirconate Ceramics Electrolyte

The role of a combination between citric acid (CA) and ethylenediaminetetra acetic acid (EDTA) as chelating agents in preparation of BaCe0.54Zr0.36Y0.1O2.95 powder by a modified sol-gel method is reported. The precursor solutions were prepared from metal nitrate salts (M

Chelating Agent Role in Synthesizing Cerate-Zirconate Powder by a Sol-Gel Method

In this study, powders of BaCe0.54Zr0.36Y0.1O2.95 (BCZY) were synthesized by a sol-gel method assisted with three different groups of chelating agents. The chelating agents used were citric acid, tartaric acid, glycolic acid from carboxylic group, tryelthylenetetraamine (TETA) from polyamino group, nitriloaacetic acid (NTA) and ethylenediaaminetetraacetic acid (EDTA) from polyamino carboxylic group. The samples were dried at 325 °C and calcined at a series of temperatures. The solution and resulting powder properties were studied using Fourier transform Infrared (FTIR) spectroscopy. FTIR spectra showed all the samples exhibit different characteristics of absorption bands after being treated at various temperatures. Such behavior indicates that the chelation process took place before the formation of metal oxide. The chelating agent from polyamino group that consists of N-donor atoms, which is TETA showed no characteristics peak of carbonates was detected after the sample was calcined at 1100 °C. Therefore, TETA gave a significant role in reducing calcination temperature for synthesizing cerate-zirconate powder.