Shen Zicai

Investigation of Laser-Induced Damage on Multi-Layer Dielectric Gratings

We investigate mechanisms of laser induced damage thresholds (LIDTs) of multi-layer dielectric gratings (AIDG,). It is found that the laser damage thresholds of MDGs and unstructured dielectric multi-layer coatings (the substrate of MDG) are 3.15J/cm(2) and 9.32 J/cm(2), respectively, at 1064nm (12ns) with the Littrow angle 51.2 degrees and the TEM00 mode. The laser-induced damage mechanism of multi-layer dielectric is presented with the analysis of the following factors: The dominant factor is the pollution on the corrugated surface, which is induced by the complex manufacture process of multi-layer dielectric gratings; another is the electric field distribution along the corrugated surface. The third reason is due to the reduction in stoichiometry of oxide films, resulting from the manufacture process of etching.

Graded Index 532HR/1064HT Filter by Glancing Angle Deposition

Glancing angle deposition is a novel method to prepare graded index coatings. By using this method and physical vapour deposition, ZrO2 is used to engineer graded index filter on BK7 glass substrate. Controlling the deposition rate and the periodic oscillation of oblique angle of deposited material, a 10-period graded index ZrO2 filter with high reflection near 532 nm and high transmittance at wavelength 1064 nm is fabricated. The causes of difference between the theoretical and experimental results are discussed in detail. The material properties and electron gun nonlinearity are possibly the main origins of the difference, which result in the variations in both thickness control and deposition rate of the Elm material.

Degradation of mechanical properties of spacecraft polyimide film exposed to radiation environments

Polyimide films are widely used in spacecraft, but their mechanical properties would degrade in radiation environments that include electrons, protons, atomic oxygen, near ultraviolet or far ultraviolet, etc. Implications of using polyimide films in spacecraft are reviewed in this paper. The degradation of mechanical properties of Kapton film exposed to electrons and far ultraviolet radiation environments were studied. It is known that the tensile strength and the rupture elongation of Kapton film decrease with the increase of the tensile deformation rate and the electron and far ultraviolet radiation. The far ultraviolet radiation will cause the rupture and cross linkage of molecular bonds in the film, deoxidation of C-CO, denitrification of C-N. The increase of C-H percentage is attributed mainly to the mechanical property degradation of Kapton film under far ultraviolet irradiation.

The Study of Simulated Space Radiation Environment Effect on Conductive Properties of ITO Thermal Control Materials

In order to prevent detrimental effects of ESD caused by differential surface charging of spacecraft under space environments, an ITO transparent conductive coating is often deposited on the thermal control materials outside spacecraft. Since the ITO coating is exposed in space environment, the environment effects on electrical property of ITO coatings concern designers of spacecraft deeply. This paper introduces ground tests to simulate space radiation environmental effects on conductive property of ITO coating. Samples are made of ITO/OSR, ITO/Kapton/Al and ITO/FEP/Ag thermal control coatings. Simulated space radiation environment conditions are NUV of 500ESH, 40 keV electron of 2 × 1016 е/cm2, 40 keV proton of 2.5 × 1015 p/cm2. Conductive property is surface resistivity measured in-situ in vacuum. Test results proved that the surface resistivity for all ITO coatings have a sudden decrease in the beginning of environment test. The reasons for it may be the oxygen vacancies caused by vacuum and decayed RIC caused by radiation. Degradation in conductive properties caused by irradiation were found. ITO/FEP/Ag exhibits more degradation than other two kinds. The conductive property of ITO/kapton/Al is stable for vacuum irradiation. The analysis of SEM and XPS found more crackers and less Sn and In concentration after irradiation which may be the reason for conductive property degradation.

Modelling analysis of influence of substrate surface defect on optical characteristics of single-layer coating

A simple and practical model is used to analyse the influence of substrate surface defect on the optical characteristics of a single-layer coating. A single-layer coating is prepared and its optical properties are fitted. Some explanations for the origin of the transition layer are presented. It is concluded that there is a transition layer forming between the substrate and coating, which is attributed to substrate surface defects, and its refractive index change is nearly of linearity.