Weikai Lei

Improved magnetic properties and thermal stabilities of Pr-Nd-Fe-B sintered magnets by Hf addition

Nd2Fe14B-type permanent magnets have been widely applied in various fields such as wind power, voice coil motors, and medical instruments. The large temperature dependence of coercivity, however, limits their further applications. We have systematically investigated the magnetic properties, thermal stabilities and coercivity mechanisms of the (Pr0.2Nd0.8)13Fe81-xB6Hfx (x=0, 0.5) nanocrystalline magnets fabricated by a spark plasma sintering (SPS) technique. The results indicate that the influence of Hf addition is significant on magnetic properties and thermal stabilities of the (PrNd)2Fe14B-type sintered magnets. It is shown that the sample with x = 0.5 at 300 K has much higher coercivity and remanent magnetization than those counterparts without Hf. The temperature coefficients of remanence (α) and coercivity (β) of the (Pr0.2Nd0.8)13Fe81-xB6Hfx magnets are improved significantly from -0.23 %/K, -0.57 %/K for the sample at x = 0 to -0.17 %/K, -0.49 %/K for the sample at x = 0.5 in the temperature range ...

Effect of Ga addition on the valence state of Ce and magnetic properties of melt-spun Ce17Fe78-xB6Gax (x = 0-1.0) ribbons

The Ce17Fe78-xB6Gax (x=0-1.0) ribbons were fabricated by a melt-spinning technique in order to study the mechanism of the valence variation of Ce and their magnetic properties as well as improve the thermal stability of Ce-based rare earth permanent magnets. The systematic investigations of the Ce17Fe78-xB6Gax (x=0-1.0) alloys show that the room-temperature coercivity increases significantly from 352 kA/m at x = 0 to 492 kA/m at x = 1.0. The Curie temperature (Tc) increases monotonically from 424.5 K to 433.6 K, and the temperature coefficients of remanence (α) and coercivity (β) of the ribbons are better off from -0.56 %/K, -0.75 %/K for x = 0 to -0.45 %/K, -0.65 %/K for x = 0.75 in the temperature range of 300–400 K, respectively. The Ce L3-edge X-ray absorption near edge structure (XANES) spectrums reveal that there is more Ce4+ in ribbons under total electron yield than fluorescence yield as Ce has a high affinity with oxygen. The weight of Ce3+ increases while the weight of Ce4+ decreases in Ga-added...