Wilfried Schuster

Transition-metal-chalcogen systems X: The Pd-Te phase diagram

The Pd-Te phase diagram has been studied in the composition range between 20 and 100 at.% Te using differential thermal analysis (DTA) and X-ray powder diffraction in combination with the results of an earlier thermodynamic investigation. In contrast with previous results by other authors it could be shown that the two phases PdTe and PdTe2, with congruent melting points at 1019 K (55.0 at.% Te) and 1025 K (66.5 at.% Te), respectively, are separated by a two-phase field at all temperatures. The phase Pd3Te2 was shown to form peritectically at 780 K. The existence of four different phases was concluded for the composition range between 25 and 30 at.% Te from the DTA results: Pd20Te7 and “Pd2.5Te”, stable up to 1026 K and 768 K, respectively; Pd9Te4, stable between 741 and 878 K, and the high temperature phase ξ, stable between 835 K and its congruent melting point at 1183 K (27.8 at.% Te). The Pd4Te phase was confirmed. Between about 20 and 25 at.% Te experimental results of the DTA measurements are reported without interpretation.

Lattice parameter and melting behavior of the ternary B2-phase in the Co-Ga-Ni system

SummaryLattice parameter and DTA-measurements were performed in the range of the ternary B2-phase in the Co-Ga-Ni system which exhibits a continuous range of homogeneity. Lattice parameter values are reported for three ternary sections with constant ratios ofxCo/xNi=0.33, 1.00, and 3.00 as well as for the two limiting binaries. Solidus and liquidus temperatures are given for 0⩽xCo/xNi⩽3.00. The results of the DTA-measurements in the Ga-Ni binary system indicate a somewhat wider range of homogeneity on the gallium-rich side as compared with literature data.ZusammenfassungIm Bereich der ternären B2-Phase im System Co-Ga-Ni, welche einen durchgehenden Homogenitätsbereich aufweist, wurden Gitterparameter bestimmt und Differenz-Thermo-Analyse durchgeführt. Werte für den Gitterparameter werden sowohl für drei ternäre Schnitte mit konstanten VerhältnissenxCo/xNi=0.33, 1.00 und 3.00 angegeben als auch für die zwei angrenzenden binären Systeme. Für 0⩽xCo/xNi⩽3.00 werden auch Solidus- und Liquidustemperaturen angegeben. Die Ergebnisse der DTA-Messungen im binären System Ga-Ni weisen auf der galliumreichen Seite — verglichen mit Literaturdaten — auf einen etwas breiteren Homogenitätsbereich hin.

Thermodynamic Properties of Iron--Selenium Alloys

Selenium vapor pressures of iron-selenium alloys were determined by an isopiestic method between 700 and 1 200 K and 50 to 60 at%Se, and activities and partial molar enthalpies of selenium were calculated. ByGibbs-Duhem integration activities of iron, and integralGibbs energies were obtained. A theoretical model was successfully applied to interprete the thermodynamic properties of the hexagonal δ-phase with NiAs-structure. Assuming a random distribution of iron vacancies in every transition metal layer of the lattice excellent agreement with experimental data was found. The energy of interaction betwen iron vacancies was calculated to be 147.0 kJ/g-atom.ZusammenfassungDie Selendampfdrücke von Eisen-Selen-Legierungen wurden mit Hilfe einer isopiestischen Methode zwischen 700 und 1 200 K und zwischen 50 und 60 At%Se bestimmt. Daraus wurden die Aktivitäten und die partiellen molaren Enthalpien von Selen berechnet, und über eineGibbs-Duhem-Integration wurden die Eisen-Aktivitäten und die integralenGibbsschen Energien erhalten. Ein theoretisches Modell wurde erfolgreich angewendet, um die thermodynamischen Eigenschaften in der hexagonalen NiAs-Phase δ zu interpretieren. Unter der Annahme einer statistischen Verteilung von Eisen-Leerstellen über sämtliche Übergangsmetall-Schichten wurde eine ausgezeichnete Übereinstimmung mit den experimentell gefundenen Daten festgestellt. Die Wechsel-wirkungsenergie zwischen diesen Leerstellen wurde zu 147,0 kJ/g-atom ermittelt.