2-stack 1D-1R Cross-point Structure with Oxide Diodes as Switch Elements for High Density Resistance RAM Applications

We have successfully integrated a 2-stack 8times8 array 1D- lR (one diode-one resistor) structure with 0.5 mumtimes0.5 mum cells in order to demonstrate the feasibility of high density stacked RRAM. p-CuOx/n-InZnOx heterojunction thin film was used for the first time as a oxide diode which shows increased current density of two orders over our previous p-NiOx/n-TiOx oxide diode. And Ti-doped NiO was used for the storage node. No limitation to the number of stacks has been observed from our results. Cell and device properties of our cross-point structure 8times8 array are reported. In addition, all fabrication processes were done at room temperature without other dedicated facilities or processes allowing for compatibility with current CMOS technology. Bi-stable switching for 1D-1R memory was demonstrated for our 2-stack cross-point structures showing excellent behavior for both diode and storage nodes. The forward current density for p-CuOx/n-IZOx diodes was over 104A/cm2, and the operation voltage for the storage node with diode attached was around 3 V.

The effects of TaN thickness and strained substrate on the performance and PBTI characteristics of poly-Si/TaN/HfSiON MOSFETs

The effects of TaN metal-gate thickness on the electrical characteristics of poly-Si/metal-gate/HfSiON MOSFETs have been investigated. Too thin TaN was reactive with poly-Si gate, which led to the formation of Si-doped metal gate. As a result, the work function of the metal gate was reduced and the capacitance increased while generating traps in HfSiON films. P-MOSFET using poly-Si/TaN gate with channel engineering in strained-Si substrate showed threshold voltage of - 0.45 V at W/L= 10/1 /spl mu/m and improved MOSFET characteristics.