Effect of transparent film desiccant on the lifetime of top-emitting active matrix organic light emitting diodes

The effects of a transparent film desiccant on the lifetime of top-emitting active matrix organic light emitting diodes (AMOLEDs) were investigated. The transparent film desiccants were prepared by mixing solutions dispersed with calcium oxide powders and ultraviolet-curable resins. As the solid content in the solutions increased from 15to30wt%, the average particle size increased from 107to240nm, whereas the transmittance of the films decreased from 98% to 80% in the visible range. The devices encapsulated with the transparent film desiccants which contained 20wt% CaO exhibited no dark spots and 97% of the initial luminance, even after being stored for over 500h at 70°C and 90% relative humidity. Also, the operational lifetime of these devices was 1850h, ten times longer than that of a device without desiccant. These results confirmed that the transparent film desiccants, which absorbed the moisture that penetrated into the devices, could be applied to the encapsulation of top-emitting AMOLEDs.