Influence of the β crystalline phase on the mechanical properties of unfilled and CaCO3-filled polypropylene. I. Structural and mechanical characterisation

Abstract The influence of β crystals on the mechanical properties of isotactic polypropylene is studied on compression-moulded sheets without filler or filled with stearate-coated calcium carbonate particles. A crystallisation procedure is setup for producing sheets with various amounts of β crystals, trying to keep constant crystallinity, spherulite size and crystal thickness. An optimum of β crystals among α crystals is first produced by isothermal crystallisation at 110°C. Then gradual transformation of β into α crystals is carried out through thermal annealing at 152°C after an intermediate cooling down to room temperature. Due to the thermal inertia of the large sheet thickness, the amount of β crystals does exceed 10% for unfilled sheets and 50% for filled sheets. Dynamic mechanical behaviour shows that molecular mobility is higher in the β crystals than in the α crystals, as judged from the temperature of the crystalline relaxation. Loss modulus in the temperature range of the crystalline relaxation also indicates greater damping capacity for the β crystals. This is discussed in terms of activation of conformational defects moving along the chain stems in the crystal. Plane strain compressive testing reveals better ductility for β rich samples. Interpretation is provided using an approach of semi-crystalline polymer plasticity based on dislocation-governed crystallographic slip. Correlation is made with the viscoelastic behaviour through the concept of conformational defects.