Journal of the American Chemical Society | 2015
Liheng Wu; Qing Li; Cheng Hao Wu; Huiyuan Zhu; Adriana Mendoza-Garcia; Bo Shen; Jinghua Guo; Shouheng Sun
Monodisperse cobalt (Co) nanoparticles (NPs) were synthesized and stabilized against oxidation via reductive annealing at 600 °C. The stable Co NPs are active for catalyzing the oxygen evolution reaction (OER) in 0.1 M KOH, producing a current density of 10 mA/cm(2) at an overpotential of 0.39 V (1.62 V vs RHE, no iR-correction). Their catalysis is superior to the commercial Ir catalyst in both activity and stability. These Co NPs are also assembled into a monolayer array on the working electrode, allowing the detailed study of their intrinsic OER activity. The Co NPs in the monolayer array show 15 times higher turnover frequency (2.13 s(-1)) and mass activity (1949 A/g) than the NPs deposited on conventional carbon black (0.14 s(-1) and 126 A/g, respectively) at an overpotential of 0.4 V. These stable Co NPs are a promising new class of noble-metal-free catalyst for water splitting.
Nano Letters | 2015
Qing Li; Liheng Wu; Gang Wu; Dong Su; Haifeng Lv; Sen Zhang; Wenlei Zhu; Anix Casimir; Huiyuan Zhu; Adriana Mendoza-Garcia; Shouheng Sun
Fully ordered face-centered tetragonal (fct) FePt nanoparticles (NPs) are synthesized by thermal annealing of the MgO-coated dumbbell-like FePt-Fe3O4 NPs followed by acid washing to remove MgO. These fct-FePt NPs show strong ferromagnetism with room temperature coercivity reaching 33 kOe. They serve as a robust electrocatalyst for the oxygen reduction reaction (ORR) in 0.1 M HClO4 and hydrogen evolution reaction (HER) in 0.5 M H2SO4 with much enhanced activity (the most active fct-structured alloy NP catalyst ever reported) and stability (no obvious Fe loss and NP degradation after 20 000 cycles between 0.6 and 1.0 V (vs RHE)). Our work demonstrates a reliable approach to FePt NPs with much improved fct-ordering and catalytic efficiency for ORR and HER.
Chemical Reviews | 2016
Liheng Wu; Adriana Mendoza-Garcia; Qing Li; Shouheng Sun
In the past two decades, the synthetic development of magnetic nanoparticles (NPs) has been intensively explored for both fundamental scientific research and technological applications. Different from the bulk magnet, magnetic NPs exhibit unique magnetism, which enables the tuning of their magnetism by systematic nanoscale engineering. In this review, we first briefly discuss the fundamental features of magnetic NPs. We then summarize the synthesis of various magnetic NPs, including magnetic metal, metallic alloy, metal oxide, and multifunctional NPs. We focus on the organic phase syntheses of magnetic NPs with precise control over their sizes, shapes, compositions, and structures. Finally we discuss the applications of various magnetic NPs in sensitive diagnostics and therapeutics, high-density magnetic data recording and energy storage, as well as in highly efficient catalysis.
Journal of the American Chemical Society | 2014
Shaojun Guo; Xu Zhang; Wenlei Zhu; Kai He; Dong Su; Adriana Mendoza-Garcia; Sally Fae Ho; Gang Lu; Shouheng Sun
Controlling the electronic structure and surface strain of a nanoparticle catalyst has become an important strategy to tune and to optimize its catalytic efficiency for a chemical reaction. Using density functional theory (DFT) calculations, we predicted that core/shell M/CuPd (M = Ag, Au) NPs with a 0.8 or 1.2 nm CuPd2 shell have similar but optimal surface strain and composition and may surpass Pt in catalyzing oxygen reduction reactions. We synthesized monodisperse M/CuPd NPs by the coreduction of palladium acetylacetonate and copper acetylacetonate in the presence of Ag (or Au) nanoparticles with controlled shell thicknesses of 0.4, 0.75, and 1.1 nm and CuPd compositions and evaluated their catalysis for the oxygen reduction reaction in 0.1 M KOH solution. As predicted, our Ag/Cu37Pd63 and Au/Cu40Pd60 catalysts with 0.75 and 1.1 nm shells were more efficient catalysts than the commercial Pt catalyst (Fuel Cells Store), with their mass activity reaching 0.20 A/mg of noble metal at -0.1 V vs Ag/AgCl (4 M KCl); this was over 3 times higher than that (0.06 A/mg Pt) from the commercial Pt. These Ag(Au)/CuPd nanoparticles are promising non-Pt catalysts for oxygen reduction reactions.
Angewandte Chemie | 2015
Adriana Mendoza-Garcia; Huiyuan Zhu; Yongsheng Yu; Qing Li; Lin Zhou; Dong Su; Matthew J. Kramer; Shouheng Sun
A facile approach to bimetallic phosphides, Co-Fe-P, by a high-temperature (300 °C) reaction between Co-Fe-O nanoparticles and trioctylphosphine is presented. The growth of Co-Fe-P from the Co-Fe-O is anisotropic. As a result, Co-Fe-P nanorods (from the polyhedral Co-Fe-O nanoparticles) and sea-urchin-like Co-Fe-P (from the cubic Co-Fe-O nanoparticles) are synthesized with both the nanorod and the sea-urchin-arm dimensions controlled by Co/Fe ratios. The Co-Fe-P structure, especially the sea-urchin-like (Co(0.54)Fe(0.46))2P, shows enhanced catalysis for the oxygen evolution reaction in KOH with its catalytic efficiency surpassing the commercial Ir catalyst. Our synthesis is simple and may be readily extended to the preparation of other multimetallic phosphides for important catalysis and energy storage applications.
Advanced Materials | 2013
Yongsheng Yu; Adriana Mendoza-Garcia; Bo Ning; Shouheng Sun
A simple process to prepare monodisperse ferrimagnetic cobalt-substituted magnetite Co(x)Fe(3-x)O4 nanoparticles is reported. These ferrimagnetic nanoparticles are readily dispersed in hexane, forming a stable ferrimagnetic nanoparticle dispersion, and allowing easy nanoparticle self-assembly. When assembled under an external magnetic field (5.5 kOe), these nanoparticles show preferred magnetic alignment with their H(c) reaching 2.49 kOe.
Nano Letters | 2017
Zheng Xi; Daniel P. Erdosy; Adriana Mendoza-Garcia; Paul N. Duchesne; Junrui Li; Michelle Muzzio; Qing Li; Peng Zhang; Shouheng Sun
We synthesize a new type of hybrid Pd/WO2.72 structure with 5 nm Pd nanoparticles (NPs) anchored on 50 × 5 nm WO2.72 nanorods. The strong Pd/WO2.72 coupling results in the lattice expansion of Pd from 0.23 to 0.27 nm and the decrease of Pd surface electron density. As a result, the Pd/WO2.72 shows much enhanced catalysis toward electrochemical oxidation of formic acid in 0.1 M HClO4; it has a mass activity of ∼1600 mA/mgPd in a broad potential range of 0.4-0.85 V (vs RHE) and shows no obvious activity loss after a 12 h chronoamperometry test at 0.4 V. Our work demonstrates an important strategy to enhance Pd NP catalyst efficiency for energy conversion reactions.
Catalysis Science & Technology | 2016
Önder Metin; Adriana Mendoza-Garcia; Diğdem Dalmizrak; Mehmet Serdar Gültekin; Shouheng Sun
Addressed herein is a facile protocol for the synthesis and assembly of FePd alloy nanoparticles (NPs) on reduced graphene oxide (rGO) to catalyze transfer hydrogenation of nitroarenes to anilines under ambient conditions. 3.5 nm FePd NPs were synthesized by using a surfactant-assisted co-reduction method that allowed NP composition control. FePd NPs were then assembled on rGO via a liquid-phase self-assembly method and studied as catalysts to promote hydrogen transfer from ammonia borane (AB) to numerous nitroarenes in aqueous methanol solutions at room temperature. Among three different rGO–FePd, the commercial C–Pd and rGO–Pd catalysts tested, rGO–Fe48Pd52 showed the highest efficiency in converting nitroarenes to anilines, achieving >90% yields within 10–20 min of reactions. Our work demonstrates an efficient and selective approach to transfer hydrogenation of nitroarenes to anilines.
Nano Letters | 2017
Bo Shen; Adriana Mendoza-Garcia; Sarah E. Baker; Scott K. McCall; Chao Yu; Liheng Wu; Shouheng Sun
We report a new strategy for stabilizing Fe nanoparticles (NPs) in the preparation of SmCo5-Fe nanocomposites. We coat the presynthesized Fe NPs with SiO2 and assemble the Fe/SiO2 NPs with Sm-Co-OH to form a mixture. After reductive annealing at 850 °C in the presence of Ca, we obtain SmCo5-Fe/SiO2 composites. Following aqueous NaOH washing and compaction, we produced exchange-coupled SmCo5-Fe nanocomposites with Fe NPs controlled at 12 nm. Our work demonstrates a successful strategy of stabilizing high moment magnetic NPs in a hard magnetic matrix to produce a nanocomposite with tunable magnetic properties.
Nanoscale | 2016
Adriana Mendoza-Garcia; Dong Su; Shouheng Sun