Nanostructures increase water droplet adhesion on hierarchically rough superhydrophobic surfaces.

Hierarchical roughness is known to effectively reduce the liquid-solid contact area and water droplet adhesion on superhydrophobic surfaces, which can be seen for example in the combination of submicrometer and micrometer scale structures on the lotus leaf. The submicrometer scale fine structures, which are often referred to as nanostructures in the literature, have an important role in the phenomenon of superhydrophobicity and low water droplet adhesion. Although the fine structures are generally termed as nanostructures, their actual dimensions are often at the submicrometer scale of hundreds of nanometers. Here we demonstrate that small nanometric structures can have very different effect on surface wetting compared to the large submicrometer scale structures. Hierarchically rough superhydrophobic TiO(2) nanoparticle surfaces generated by the liquid flame spray (LFS) on board and paper substrates revealed that the nanoscale surface structures have the opposite effect on the droplet adhesion compared to the larger submicrometer and micrometer scale structures. Variation in the hierarchical structure of the nanoparticle surfaces contributed to varying droplet adhesion between the high- and low-adhesive superhydrophobic states. Nanoscale structures did not contribute to superhydrophobicity, and there was no evidence of the formation of the liquid-solid-air composite interface around the nanostructures. Therefore, larger submicrometer and micrometer scale structures were needed to decrease the liquid-solid contact area and to cause the superhydrophobicity. Our study suggests that a drastic wetting transition occurs on superhydrophobic surfaces at the nanometre scale; i.e., the transition between the Cassie-Baxter and Wenzel wetting states will occur as the liquid-solid-air composite interface collapses around nanoscale structures. Consequently, water adheres tightly to the surface by penetrating into the nanostructure. The droplet adhesion mechanism presented in this paper gives valuable insight into a phenomenon of simultaneous superhydrophobicity and high water droplet adhesion and contributes to a more detailed comprehension of superhydrophobicity overall.

Paper-based microfluidics: fabrication technique and dynamics of capillary-driven surface flow.

Paper-based devices provide an alternative technology for simple, low-cost, portable, and disposable diagnostic tools for many applications, including clinical diagnosis, food quality control, and environmental monitoring. In this study we report a two-step fabrication process for creating two-dimensional microfluidic channels to move liquids on a hydrophobized paper surface. A highly hydrophobic surface was created on paper by TiO2 nanoparticle coating using a high-speed, roll-to-roll liquid flame spray technique. The hydrophilic pattern was then generated by UV irradiation through a photomask utilizing the photocatalytic property of TiO2. The flow dynamics of five model liquids with differing surface tensions 48-72 mN·m(-1) and viscosities 1-15 mN·m(-2) was studied. The results show that the liquid front (l) in a channel advances in time (t) according to the power law l=Zt0.5 (Z is an empirical constant which depend on the liquid properties and channel dimensions). The flow dynamics of the liquids with low viscosity show a dependence on the channel width and the droplet volume, while the flow of liquids with high viscosity is mainly controlled by the viscous forces.

Adhesion mechanism of water droplets on hierarchically rough superhydrophobic rose petal surface

Extremely hydrophobic surfaces, on which water droplets sit in a spherical shape leaving air entrapped into the roughness of the solid, are often called superhydrophobic. Hierarchically rough superhydrophobic surfaces that possess submicron scale fine structures combined with micron scale structures are generally more hydrophobic, and water droplet adhesion to those surfaces is lower in comparison with surfaces possessing purely micrometric structures. In other words, usually a fine structure on a superhy-drophobic surface reduces liquid-solid contact area and water droplet adhesion. Here we show that this does not apply to a high-adhesive superhydrophobic rose petal surface. Contrary to the present knowledge, the function of the fine structure on the petal surface is to build up the high adhesion to water droplets. Understanding of the specific adhesion mechanism on the rose petal gives insight into an interesting natural phenomenon of simultaneous superhydrophobicity and high water droplet adhesion, but, in addition, it contributes to more precise comprehension of wetting and adhesion mechanisms of superhydrophobic surfaces overall.

Nanoparticle Deposition from Liquid Flame Spray onto Moving Roll-to-Roll Paperboard Material

Nanostructured coatings have been prepared on a flexible, moving paperboard using deposition of ca. 40-nm-sized titanium dioxide nanoparticles generated by a liquid flame spray process, directly above the paperboard, to achieve improved functional properties for the material. Properties such as surface wettability can be extensively improved by a thin layer of nanoparticles on the substrate. Owing to the vulnerability to heat, the substrate needs to be moved rapidly through the flame. This, on the other hand, generates a setting for a roll-to-roll coating process, which favors upscaling of the method. In this article, we characterize the flame process for nanoparticle coating and quantify the operational window for this method. The amount of deposited material as a function of substrate speed through the flame is discussed. Although the thermophoretic flux of nanoparticles is estimated to be very high from the hot flame onto the cold substrate, other factors were observed to limit the deposited amount of particles. Total mass yields of 5%–20% of the injected precursor material into the titanium dioxide nanocoating on the paperboard were achieved. With these yields, a highly hydrophobic surface was obtained by a mass loading of 10–50 mg/m2 of titanium dioxide on the paperboard.

Roll-to-roll atomic layer deposition process for flexible electronics encapsulation applications

At present flexible electronic devices are under extensive development and, among them, flexible organic light-emitting diode displays are the closest to a large market deployment. One of the remaining unsolved challenges is high throughput production of impermeable flexible transparent barrier layers that protect sensitive light-emitting materials against ambient moisture. The present studies deal with the adaptation of the atomic layer deposition (ALD) process to high-throughput roll-to-roll production using the spatial ALD concept. We report the development of such a process for the deposition of 20 nm thickness Al2O3 diffusion barrier layers on 500 mm wide polymer webs. The process uses trimethylaluminum and water as precursors at a substrate temperature of 105 °C. The observation of self-limiting film growth behavior and uniformity of thickness confirms the ALD growth mechanism. Water vapor transmission rates for 20 nm Al2O3 films deposited on polyethylene naphthalate (PEN) substrates were measured a...

ToF-SIMS analysis of UV-switchable TiO2-nanoparticle-coated paper surface.

The chemical composition of a TiO2 nanoparticle coated paper surface was analyzed using time-of-flight secondary ion mass spectrometry (ToF-SIMS) to study the interconnection between wettability and surface chemistry on the nanoscale. In this work, a superhydrophobic TiO2 surface rich in carboxyl-terminated molecules was created by a liquid flame spray process. The TiO2 nanoparticle coated paper surface can be converted by photocatalytic oxidation into a highly hydrophilic one. Interestingly, the hydrophilic surface can be converted back into a superhydrophobic surface by heat treatment. The results showed that both ultraviolet A (UVA) and oven treatment induce changes in the surface chemistry within a few nanometers of the paper surface. These findings are consistent with those from our previously reported X-ray photoelectron spectroscopy (XPS) analysis, but the ToF-SIMS analysis yields more accurate insight into the surface chemistry.

Wettability conversion on the liquid flame spray generated superhydrophobic TiO 2 nanoparticle coating on paper and board by photocatalytic decomposition of spontaneously accumulated carbonaceous overlayer

Titanium dioxide (TiO2) is a photoactive material with various interesting and useful properties. One of those is the perfect wettability of TiO2 surface after ultraviolet (UV) illumination. Wettability of a solid surface plays an important role in the field of printing, coating, and adhesion among others. Here we report on a superhydrophobic and photoactive liquid flame spray (LFS) generated TiO2 nanoparticle coating that can be applied on web-like materials such as paper and board in one-step roll-to-roll process. The LFS TiO2 nanoparticle coated paper and board were superhydrophobic instantly after the coating procedure because of spontaneously accumulated carbonaceous overlayer on TiO2, and thus there was no need for any type of separate hydrophobization treatment. The highly photoactive LFS TiO2 nanoparticle coating could be converted steplessly from superhydrophobic to superhydrophilic by UV-illumination, and the coating gave strong response to natural daylight illumination even in the shade. The superhydrophobic LFS TiO2 coated surface can be used as an intelligent substrate, where photo-generated hydrophilic patterns guide the fluid setting and figure formation. Our study reveals that the wettability changes on the LFS TiO2 surface were primarily caused by the photocatalytic removal of the carbonaceous material from TiO2 during the UV-illumination and spontaneous accumulation of the carbonaceous material on the surface of the metal oxide during storage in the dark. The latter mechanism was found to be a temperature activated process which could be significantly speeded up by heat treatment. If other mechanisms such as surface oxidization, increment of hydroxyl groups, or charge separation played a role in the wetting phenomena on TiO2, their effect was rather secondary as the removal and accumulation of the carbonaceous material dominated the wettability changes on the surface. Our study gives valuable information on the complex issue of photo-induced wettability changes on TiO2.

The Influence of Flame, Corona and Atmospheric Plasma Treatments on Surface Properties and Digital Print Quality of Extrusion Coated Paper

Polymer and paper structures have been successfully utilized in several fields, especially in the packaging industry. Together with barrier properties, printability is an important property in packaging applications. From the point of view of printing, the dense and impervious structure of extrusion coatings is challenging. Flame, corona and atmospheric plasma treatments were used to modify the surface of low density polyethylene (LDPE) and polypropylene (PP) and the influence of these surface modifications on print quality, i.e., toner adhesion and visual quality was studied. The traditional surface treatment methods, i.e., flame and corona treatments, increased the surface energy by introducing oxygen containing functional groups on the surfaces of LDPE and PP more than helium and argon plasma treatments. Only in the case of flame treatment, the higher surface energy and oxidation level led to better print quality, i.e., toner adhesion and visual quality, than the plasma treatments. The morphological changes observed on LDPE surface after flame treatment are partly responsible for the improved print quality. Atmospheric plasma treatments improved the print quality of LDPE and PP surfaces more than corona treatment. The electret phenomenon observed on LDPE and PP surfaces only after corona treatment is the most likely reason for the high print mottling and low visual quality of corona treated surface.

Low temperature temporal and spatial atomic layer deposition of TiO2 films

Titanium dioxide films were grown by atomic layer deposition (ALD) using titanium tetraisopropoxide as a titanium precursor and water, ozone, or oxygen plasma as coreactants. Low temperatures (80–120 °C) were used to grow moisture barrier TiO2 films on polyethylene naphthalate. The maximum growth per cycle for water, ozone, and oxygen plasma processes were 0.33, 0.12, and 0.56 A/cycle, respectively. X-ray photoelectron spectrometry was used to evaluate the chemical composition of the layers and the origin of the carbon contamination was studied by deconvoluting carbon C1s peaks. In plasma-assisted ALD, the film properties were dependent on the energy dose supplied by the plasma. TiO2 films were also successfully deposited by using a spatial ALD (SALD) system based on the results from the temporal ALD. Similar properties were measured compared to the temporal ALD deposited TiO2, but the deposition time could be reduced using SALD. The TiO2 films deposited by plasma-assisted ALD showed better moisture barri...

Creation of superhydrophilic surfaces of paper and board

Corona, flame, atmospheric plasma, and liquid flame spray (LFS) techniques were used to create highly hydrophilic surfaces for pigment-coated paper and board and machine-glossed paper. All the surface modification techniques were performed continuously in ambient atmosphere. The physical changes on the surfaces were characterized by field emission gun-scanning electron microscopy (FEG-SEM), atomic force microscopy and Parker Print-Surf surface roughness. The chemical changes were analysed by X-ray photoelectron spectroscopy. The superhydrophilic surfaces, i.e. contact angle of water (CAW) <10°, were created mainly by modifying the surface chemistry of the paper and board by argon plasma or SiO2 coating. The nano- and microscale roughness existing on paper and board surfaces enabled the creation of the superhydrophilic surfaces. Furthermore, the benefits and limitations of the surface modification techniques are discussed and compared. For example, the SiO2 coating maintained its extreme hydrophilicity for at least six months, whereas the CAW of argon plasma-treated surface increased to about 20° already in one day.