Novel green nano composites films fabricated by indigenously synthesized graphene oxide and chitosan.

Graphene oxide (GO) was indigenously synthesized from graphite using standard Hummers method. Chitosan-graphene oxide green composite films were fabricated by mixing aqueous solution of chitosan and GO using dilute acetic acid as a solvent for chitosan. Chitosan of different viscosity and calculated molecular weight was used keeping amount of GO constant in each composite film. The structural properties, thermal stability and mechanical properties of the composite films were investigated using Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and tensile test. FTIR studies revealed the successful synthesis of GO from graphite powder and it was confirmed that homogenous blending of chitosan and GO was promising due to oxygenated functional groups on the surface of GO. XRD indicated effective conversion of graphite to GO as its strong peak observed at 11.06° as compared to pristine graphite which appeared at 26°. Moreover, mechanical analysis confirmed the effect of molecular weight on the mechanical properties of chitosan-GO composites showing that higher molecular weight chitosan composite (GOCC-1000) showed best strength (higher than 3GPa) compared to other composite films. Thermal stability of GOCC-1000 was enhanced for which residual content increased up to 56% as compared to the thermal stability of GOCC-200 whose residue was restricted to only 24%. The morphological analysis of the composites sheets by SEM was smooth having dense structure and showed excellent interaction, miscibility, compatibility and dispersion of GO with chitosan. The prepared composite films find their applications as biomaterials in different biomedical fields.

An Investigation of Ac Impedance and Dielectric Spectroscopic Properties of Conducting Chitosan-silane Crosslinked-poly (Vinyl Alcohol) Blended Films

The films of chitosan (CS)-silane crosslinked-poly(vinyl alcohol) (PVA) with different weight % were prepared. The effect on conductivity of CS/PVA blended films due to change in the concentration of PVA and temperature was investigated by impedance spectroscopy and showed good conductance properties. The complex impedance plots revealed single semicircular arcs indicating the bulk contribution to overall electrical behavior of all synthesized samples. The ac conductivity obeyed the Jonschers power law for all samples in the frequency range of 2 kHz to 2 MHz. The ionic conductivity of the films was increased with the increase in temperature for all synthesized samples which showed an increase in the number of effective charge carriers while it was decreased at a specific higher temperature for each film. The observed activation energy for CP4, CP8 and CP10 were 0.431, 0.610 and 0.425 eV, respectively. These properties showed that the films were promising materials to be employed for conducting properties.