R. Douglas

Cryogenic and room temperature strength of sapphire jointed by hydroxide-catalysis bonding

Hydroxide-catalysis bonding is a precision technique used for jointing components in opto-mechanical systems and has been implemented in the construction of quasi-monolithic silica suspensions in gravitational wave detectors. Future detectors are likely to operate at cryogenic temperatures which will lead to a change in test mass and suspension material. One candidate material is mono-crystalline sapphire. Here results are presented showing the influence of various bonding solutions on the strength of the hydroxide-catalysis bonds formed between sapphire samples, measured both at room temperature and at 77 K, and it is demonstrated that sodium silicate solution is the most promising in terms of strength, producing bonds with a mean strength of 63 MPa. In addition the results show that the strengths of bonds were undiminished when tested at cryogenic temperatures.

Field Tests of a Portable MEMS Gravimeter

Gravimeters are used to measure density anomalies under the ground. They are applied in many different fields from volcanology to oil and gas exploration, but present commercial systems are costly and massive. A new type of gravity sensor has been developed that utilises the same fabrication methods as those used to make mobile phone accelerometers. In this study, we describe the first results of a field-portable microelectromechanical system (MEMS) gravimeter. The stability of the gravimeter is demonstrated through undertaking a multi-day measurement with a standard deviation of 5.58×10−6 ms−2. It is then demonstrated that a change in gravitational acceleration of 4.5×10−5 ms−2 can be measured as the device is moved between the top and the bottom of a 20.7 m lift shaft with a signal-to-noise ratio (SNR) of 14.25. Finally, the device is demonstrated to be stable in a more harsh environment: a 4.5×10−4 ms−2 gravity variation is measured between the top and bottom of a 275-m hill with an SNR of 15.88. These initial field-tests are an important step towards a chip-sized gravity sensor.

The effect of crystal orientation on the cryogenic strength of hydroxide catalysis bonded sapphire

Hydroxide catalysis bonding has been used in gravitational wave detectors to precisely and securely join components of quasi-monolithic silica suspensions. Plans to operate future detectors at cryogenic temperatures has created the need for a change in the test mass and suspension material. Mono-crystalline sapphire is one candidate material for use at cryogenic temperatures and is being investigated for use in the KAGRA detector. The crystalline structure of sapphire may influence the properties of the hydroxide catalysis bond formed. Here, results are presented of studies of the potential influence of the crystal orientation of sapphire on the shear strength of the hydroxide catalysis bonds formed between sapphire samples. The strength was tested at approximately 8 K; this is the first measurement of the strength of such bonds between sapphire at such reduced temperatures. Our results suggest that all orientation combinations investigated produce bonds of sufficient strength for use in typical mirror suspension designs, with average strengths >23 MPa.

Microelectromechanical system gravimeters as a new tool for gravity imaging

A microelectromechanical system (MEMS) gravimeter has been manufactured with a sensitivity of 40 ppb in an integration time of 1 s. This sensor has been used to measure the Earth tides: the elastic deformation of the globe due to tidal forces. No such measurement has been demonstrated before now with a MEMS gravimeter. Since this measurement, the gravimeter has been miniaturized and tested in the field. Measurements of the free-air and Bouguer effects have been demonstrated by monitoring the change in gravitational acceleration measured while going up and down a lift shaft of 20.7 m, and up and down a local hill of 275 m. These tests demonstrate that the device has the potential to be a useful field-portable instrument. The development of an even smaller device is underway, with a total package size similar to that of a smartphone. This article is part of a discussion meeting issue ‘The promises of gravitational-wave astronomy’.

Determination of the refractive index and thickness of a hydroxide-catalysis bond between fused silica from reflectivity measurements

Hydroxide-catalysis bonding is a high precision jointing technique producing strong, transparent and thin bonds, the use of which in the delicate fused silica mirror suspensions of aLIGO have been instrumental in the first detections of gravitational radiation. More sensitive future gravitational wave detectors will require more accurate (ideally in situ) measurements of properties such as bond thickness. Here a non-destructive technique is presented in which the thickness and refractive index of a bond are determined from measurements of optical reflectivity. The reflectivity of a bond made between two fused silica discs using sodium silicate solution is less than 1⋅10-3 after 3 months. The thickness decreases to a constant value of around 140 nm at its minimum and the refractive index increases from 1.36 to 1.45. This proves that as well as determination of bond thickness in situ this bonding technique is highly interesting for optical applications.