S.L. Feng

Effect of InxGa1−xAs (0⩽x⩽0.4) capping layer on self-assembled 1.3 μm wavelength InAs/GaAs quantum islands

We report the effect of InchiGa1-chiAs (0 less than or equal to chi less than or equal to0.4) capping layer on photoluminescence (PL) properties of 1.3 mum wavelength self-assembled InAs quantum islands, which are formed via depositing 3.5 monolayers (ML) InAs on GaAs (1 0 0) substrate by molecular beam epitaxy (MBE). Compared with the InchiGa1-chiAs capping layer containing a larger In mole fraction chi greater than or equal to0.2 and the GaAs capping layer (chi = 0), the InAs islands covered by the In0.1Ga0.9As layer show PL with lower emission energy, narrower full-width at half-maximum (FWHM), and quite stronger intensity. The PL peak energy and FWHM become more temperature dependent with the increase of In content in the InchiGa1-chiAs capping layer (chi greater than or equal to0.2), while the InAs islands covered by the In0.1Ga0.9As layer is much less temperature sensitive. In addition, the InAs islands covered by the In0.1Ga0.9As capping layer show room temperature PL wavelength at about 1.3 mum

Photoluminescence in Si and Be directly doped self-organized InAs/GaAs quantum dots

We report on the photoluminescence in directly Si- and Be-doped self-organized InAs/GaAs quantum dots (QDs). When the doping level is low, a decrease in linewidth is observed. However, it will decrease the uniformity and photoluminescence peak intensity of QDs when the doping level is high. We relate this phenomenon to a model that takes the Si or Be atoms as the nucleation centers for the formation of QDs

1.35 μm photoluminescence from In0.5Ga0.5As/GaAs islands grown by molecular beam epitaxy via cycled (InAs)1/(GaAs)1 monolayer deposition

1.35 mum photoluminescence (PL) with a narrow linewidth of only 19.2 meV at room temperature has been achieved in In0.5Ga0.5As islands structure grown on GaAs (1 0 0) substrate by solid-source molecular beam epitaxy. Atomic force microscopy (AFM) measurement reveals that the 16-ML-thick In0.5Ga0.5As islands show quite uniform InGaAs mounds morphology along the [ 1(1) over bar 0] direction with a periodicity of about 90 nm in the [1 1 0] direction. Compared with the In0.5Ga0.5As alloy quantum well (QW) of the same width, the In0.5Ga0.5As islands structure always shows a lower PL peak energy and narrower full-width at half-maximum (FWHM), also a stronger PL intensity at low excitation power and more efficient confinement of the carriers. Our results provide important information for optimizing the epitaxial structures of 1.3 mum wavelength quantum dots devices

Surface morphology and optical property of 1.3 mu m In0.5Ga0.5As/GaAs self-organized quantum dots grown by MBE

Surface morphology and optical properties of 1.3 mum self-organized InGaAs/GaAs quantum dots structure grown by molecular beam epitaxy have been investigated by atomic force microscopy and photoluminescence measurements. It has been shown that the surface morphology evolution and emission wavelengths of InGaAs/GaAs QDs can be controlled effectively via cycled monolayer deposition methods due to the reduction of the surface strain. Our results provide important information for optimizing the epitaxial parameters for obtaining 1.3 mum long wavelength emission quantum dots structures

Role of different cap layers tuning the wavelength of self-assembled InAs/GaAs quantum dots

We have investigated the effect of different cap layers on the photoluminescence (PL) of self-assembled InAs/GaAs quantum dots (QDs). Based upon different cap layers, the wavelength of InAs QDs can be tuned to the range from 1.3 to 1.5 mum. An InAlAs and InGaAs combination layer can enlarge the energy separation between the ground and first excited radiative transition. GaAs/InAs short period superlattices (SLs) make the emission wavelength shift to 1.53 mum. The PL intensity of InAs QDs capped with GaAs/InAs SLs shows an anomalous increase with increasing temperature. We attribute this to the transfer of carriers between different QDs.

The fabrication of self-aligned InAs nanostructures on GaAs(331)A substrates

Self-aligned InAs quantum wires (QWRs) or three-dimensional (3D) islands are fabricated on GaAs(331)A substrates by molecular beam epitaxy (MBE). InAs QWRs are selectively grown on the step edges formed by GaAs layers. The surface morphology of InAs nanostructures is carefully investigated by atomic force microscopy (AFM) measurements. Different growth conditions, such as substrate temperature, growth approaches, and InAs coverage, exert a great effect on the morphology of InAs islands. Low substrate temperatures favour the formation of wirelike nanostructures, while high substrate temperatures favour 3D islands. The shape transition is attributed to the trade-off between surface energy and strain energy. A qualitative agreement of our experimental data with the theoretical results derived from the model proposed by Tersoff and Tromp is achieved.

Formation of InAs quantum dots on low-temperature GaAs epi-layer

InAs self-organized quantum dots (QDs) grown on annealed low-temperature GaAs (LT-GaAs) epi-layers and on normal temperature GaAs buffer layers have been compared by transmission electron microscopy (TEM) and photoluminescence (PL) measurements. TEM evidences that self-organized QDs were formed with a smaller size and larger density than that on normal GaAs buffer layers. It is discussed that local tensile surface strain regions that are preferred sites for InAs islands nucleation are increased in the case of the LT-GaAs buffer layers due to exhibiting As precipitates. The PL spectra show a blue-shifted peak energy with narrower linewidth revealing the improvement of optical properties of the QDs grown on LT-GaAs epi-layers. It suggests us a new way to improve the uniformity and change the energy band structure of the InAs self-organized QDs by carefully controlling the surface stress states of the LT-GaAs buffers on which the QDs are formed