Enhanced Optical and Electrical Properties of ITO/Ag/AZO Transparent Conductors for Photoelectric Applications

The enhancement of the optical and electrical properties of TCO films was investigated by depositing different layers of AZO (100 nm), Ag (5 nm)/AZO (95 nm), and ITO (45 nm)/Ag (5 nm)/AZO (50 nm) upon n-Si substrate at room temperature by magnetron sputtering method. The ITO/Ag/AZO device efficiently improved the electrical and optical properties with the low sheet resistance of 2.847 Ω/sq. and an increase in the rectification ratio of 455.60% when compared with AZO and Ag/AZO devices. The combination of ITO/Ag/AZO provided the optimum results in all the electrical and optical properties. These results showed that within the optimized thickness range of 100 nm, compared to AZO and Ag/AZO, ITO/Ag/AZO device showed the improvement for both optical and electrical properties at room temperature.

Sample preparation and electrochemical data of Co3O4 working electrode for seawater splitting

In this data article, we presented the electrochemical data of the working electrode made of Co3O4 semi-transparent film. Electrochemically stable, porous nature of Kirkendall-diffusion grown Co3O4 films were applied to generate hydrogen from the seawater splitting (Patel et al., 2017) [1]. The data presented in this article includes the photograph of prepared samples, polarization curves for water oxidation and Tafel plot, linear sweep voltammetry measurements under the pulsed light condition in 0.1 M Na2S2O3 electrolyte, and transient photoresponses with natural sea water. Moreover, seawater splitting using the Co3O4 working electrode is demonstrated.