Electrical quadruple hysteresis in Pd-doped vanadium pentoxide nanowires due to water adsorption

Abstract Humidity-dependent current–voltage (I–V) characteristics of Pd-doped vanadium pentoxide nanowires (Pd-VONs) were investigated. Electrical quadruple hysteresis (QH) was observed and attributed to the large amount of water molecules adsorbed on the nanowires. Using QH in Pd-VONs, the reaction of water with PdO was interpreted as the water molecules are desorbed and then dissociated with increasing bias voltage. Owing to the dissociated H+ and OH− ions, PdO is reduced and oxidized. As a result, water molecules recombine as the bias voltage is decreased.

The Observation of electrical hysteric behavior in synthesized V 2 O 5 nanoplates by recrystallization

The anomalous electrical conductance for the V2O5 foam synthesized via a foaming process was measured. In the annealing process, the synthesized V2O5 foamis recrystallized with the increase of annealing temperature. The recrystallization procedure was characterized by using physical analysis tools such as thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), and X-ray diffractometer. In the electrical analysis technique of current-voltage characteristics as a function of annealing temperature, an anomalous hysteric behavior appears at the annealing temperature of 400°C. We conclude that the recrystallization of V2O5 nanoplates results in the anomalous behavior in voltage-dependent current characteristics.