Jung-Hwan Hah

Strategy for sub-80-nm contact hole patterning considering device fabrication

As the required contact holes dimension (CD) reaches to the physical limit of the conventional lithography, the image quality formed in a photoresist film is degraded seriously. To overcome this obstacle, several process-based techniques for ArF lithography have been suggested and some of them are reported to show excellent feasibilities. In this article, three primary techniques for sub-80nm contact holes patterning are examined. They are ArF thermal flow, ArF SAFIER (Shrink Assist Film for Enhanced Resolution) and ArF RELACS (Resolution Enhancement Lithography Assisted by Chemical Shrink). These techniques are originated from different reaction mechanisms and result in distinguished shrink behaviors. Contact holes CDs of different patterns diverge one another depending on the adapted shrink process even though the initial CDs are identical. This is so called a bulk effect and is compensated by the optical proximity correction (OPC) procedure. The relationship of pattern CDs between mask and wafer is used to extract the correction factor. For the shrink process, it is divided to an optical factor and a process factor, that is, the shrink behavior is analyzed in terms of mask error factor (MEF) and process error factor (PEF). The PEF is calculated from the proportionality of post-shrink CD to initial CD of photoresist patterns. Using the PEF, it is possible to characterize each shrink process in the view of CD controllability. Consequently, we classify the shrink processes for the production of 65nm node devices considering the shrink properties and the cost of ownership.

Top barrier coating materials for immersion lithography and beyond

Immersion barrier coats were formulated and evaluated on ArF photoresist in view of interaction between photoresist and top coats. Acrylate polymers having an acid-labile protecting group, an acid group, and a polar group were synthesized to realize water barrier property and developability. To compensate the insufficient developability, thermal acid generator was included as an additive that can enhance the developability of the acrylate top coats by post exposure bake. In the course of the material evaluation, it became evident that carboxyl acid group in the top coat base polymers has great influence on photoresist profiles, and this result was fedback to a new acid group, deuterated carboxyl acid, that is suitable for both ArF wavelength and EUV wavelength. When top coat materials having deuterated carboxyl acid were applied on ArF photoresist, fine pattern profiles were confirmed. Further, an extension of barrier coating concept to EUV lithography as outgas barrier coats was examined on an EUV photoresists test sample. These outgas barrier coat materials do not include fluorine atoms, therefore, achieves good transparency at EUV wavelength.

Novel chemical shrinkage material for small contact hole and small space patterning

It is becoming difficult for the lithography progress to keep pace with the acceleration of design rule shrinkage and high integration of memory devices. In order to retain the acceleration, low k1 processes beyond the limitation of wavelength are required. Various resolution enhancement techniques have been suggested for this purpose. Especially, chemical shrinkage process utilizing an additional chemical treatment upon patterned photoresist to make patterns finer has been turned out to be effective. The current chemical shrinkage materials are, however, suffering from small attachment amounts or pattern deformation. In this paper, a novel chemical shrinkage material causing large attachments without pattern deformation is suggested. The material is an aqueous solution of two kinds of polymers and its shrinkage mechanism is based on inter-polymer complex formation and gelation principle. Compositions, shrinkage properties, and application studies to contact hole patterns are presented.

Chemical shrinkage material: Nanoscale patterning through interpolymer complex

A chemical shrinkage material causing large attachments without pattern deformation is suggested. This material is an aqueous solution of two kinds of polymers, and its shrinkage mechanism is based on the interpolymer complex formation and gelation principle. Attachment greater than 25nm was confirmed on ArF photoresist pattern at 145°C, and its shrinkage properties were found to be proportional to initial critical dimension and process temperature, and pitch dependency was not observed. An additional study on temperature responsive phase transition behavior of the material was also undertaken.